Damage

8 cases · 37 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Offshore Detail focus: Sampling and Analysis clear all

Damage — sub-branches

Brittle Behavior 1Corrosion 4Fabrication Defect 3Fatigue 1Hydrogen 1

Results

SortNewestOldestTitle A-ZTitle Z-A
The location of the threaded fitting started leaking after less than five years in service. Although the corrosion rate was not high, the localized material loss in the threaded surface of the carbon steel flange allowed the connection leakage.
770
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Aspect Before AnalysisDf - General View
Aspect of the hydraulic cylinder, new, stored in tropical conditions under a plastic cover, that allowed a condensation condition and damage.
92
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Aspect Before AnalysisDf - General View
Aspect of the 5/8" diameter pin, that was 3" long and broke close to the center.
104
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Macrography of the fillet welded joint between the 3" ND tube and the 3/4" thick plate. See the schematic drawing in the next figure
56
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint
General view of the 2" branch line that was supporting an instrument in a 12" gas piping of an offshore unity. The branch line is composed by a seamless pipe welded to a weldolet (left side of the figure) and to a flange (right side of the figure). The leakage is associated to a through wall cracking in the middle of the pipe length. The cracking is not evidenced in the figure, since it is too thin. See the schematic drawing in the next figure
494
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - General View
Fracture appearance of the 1 1/4" diameter link. The fracture is flat and presented no evidences of plastic deformation, suggesting a brittle behavior.
54
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Tempered martensitic structure of the plate base metal.
93
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal
Visual aspect of the 3/8" diameter pin surface, presenting several lozalized corrosion spots.
53
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - At the Surface

More from these cases

ML00184 — Dissimilar Steels in a Threaded ConnectionM - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
The cleaned fitting is sound. No corrosion, only surface stains.
121
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Aspect After CleaningDf - General View
Micrography of the valve body carbon steel thread, in the valley. Ferritic-bainitic structure.
77
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Transverse Section
ML00128 — MIC of a Stored Hydraulic CylinderM - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Aspect of the hydraulic cylinder surface presenting white stains in a region where the damage was still in the begining.
73
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Aspect Before AnalysisDf - External Surface
As polished micrographic aspect of the longitudinal section of the cylinder, at the surface, in a region where the damage is in the begining. It is possible to see that there are two layers at the surface. A first Ni layer, 300HV average hardness, over the low carbon steel substrate, 200HV average hardness, and a chromium plated layer, 1100HV average hardness and several discontinuities.
62
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Micrography by OMDf - Longitudinal Section
Detail of a localized dissolution at the surface of the chromium plated cylinder. Note the dimension of the corrosion pitting, shallow.
33
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Aspect Before AnalysisDf - At the Surface
Scanning electron microscopy image of the chromium plated surface in a position where the cylinder was not damaged, showing the surface finishing.
35
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Surface Aspect by SEMDf - At the Surface
ML00052 — Cold Cracks in API 5CT L80 Tube Welded to a Structural PartM - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Schematic drawing presenting the position of the cracking, at the margin of the weld in the tube and underbead.
47
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Identification drawingDf - Welded Joint
Low carbon plate base metal presenting the ferritic perlitic structure.
55
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal
High Strenght Low Alloy steel tube, base metal, presenting the bainitic structure.
54
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of the low carbon steel plate at the fusion line, presenting a bainitic structure at the HAZ and ferritic structure in the weld metal.
82
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Fusion Line
Micrography of the weld metal in the center of the fillet showing a 100% acicular ferrite that is a microestructure of a high strenght steel, evidenced the effect of the dilution of the tube chemistry in the weld metal.
40
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Weld Metal

+6 more from this case →

ML00012 — Vibration Induced Fatigue in a 316/316L SSM - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Schematic drawing presenting the general view of the 2" branch line that was supporting an instrument in a 12" gas piping of an offshore unity.
94
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Identification drawingDf - General View
Aspect of the internal surface of the pipe after longitudinal cutting, presenting a straight cracking, circumferential. The weldolet is to the left side and the flange is to the right side. See the schematic drawing in the next figure.
89
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface
Schematic drawing presenting the cracking surface aspect.
71
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Identification drawingDf - Internal Surface
Circumferential cracking in the middle of the pipe, view from the external side. Several pits close to the cracking.
57
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - External Surface
Pipe view from the external side. Pitting corrosion.
42
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Surface Aspect by SEMDf - External Surface
ML00079 — Hydrogen Cracking of a Maritime Chain LinkM - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Macrography of the longitudinal section of the broken link, at the fracture surface. There are several secondary cracks, parallel and perpendicular to the link axis.
38
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Longitudinal Section AspectDf - Longitudinal Section
ML00010 — Cold Cracks in a Gouged Weld MetalM - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Detail of the tempered martensitic structure of the plate base metal. Hardness level of 27 HRc.
92
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal
Low magnification micrography of a transverse section of the weld at the heat affected zone region. The macrosection was hardness tested and the base metal hardness is 27HRc, the HAZ is 32HRc and the weld metal is 45HRc, revealing something wrong in the weld metal at the position close to the cracked area.
79
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Transverse Section
High temperature heat affected zone of the plate, welded in repair. The micrography was taken from a sample collected close to the cracked region, but not containing any macroscopic cracking.
76
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Detail of the high temperature heat affected zone of the plate, welded in repair.
69
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
The weld metal, hard, presented a martensitic structure, probably due to the localized increase in carbon content, from the unsuitable carbon arc gouging procedure.
63
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Weld Metal

+1 more from this case →