Hydrogen

10 cases · 24 images for “brittle fracture”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
The main crack is to the top and the blade surface is to the right, in this micrography that does not reveal any plastic deformation, with transgranular and integranular cracks.
24
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Brittle Fracture
Aspect of the bolt fracture, presenting a flat surface.
80
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Fracture Surface AspectDf - Brittle Fracture
Macroscopic view of the fracture surface showing that there is a flat appearance of the fracture close to the bottom of the thread (upper side of the figure) and a flat, but rough appearance in the center of the stud. No evidences of corrosion in the thread fillets indicating that the stud was protected.
59
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Brittle Fracture
Aspect of the broken pin after removal from the box end.
125
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Brittle Fracture
Scanning electron fractography of a chromium plated pin, close to the pin surface where the fatigue cracking started, showing intergranular morphology typical of a hydrogen embrittlement effect. It occurred because the low alloy pin was carburized, quenched and tempered, with a too high hardness structure, before the electrolytic plating.
837
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
Aspect of the fracture surface of the pin, still assembled in the box (that is externally to the pin). The pin fracture is flat, presenting radial marks.
791
VIEW
ML00088 / Dec.2017
Hydrogen Cracking of an API 5D S135 Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Brittle Fracture
Detail of the fracture surface, predominantly transgranular with secondary cracks of intergranular morphology.
831
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
The spring presents intergranular and transgranular brittle aspects in the fracture surface.
884
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture

More from these cases

ML00139 — Hydrogen Fracture of a 17-4 PH Allen BoltM - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
The fracture, that occurred at the region of transition between the threaded body and the bolt head, presented a flat and brittle aspect.
69
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Fracture Surface AspectDf - Brittle Fracture
Micrography of a longitudinal section of the bolt, close to the fracture surface (top of the figure). The fracture is macroscopically flat and started at the surface (left side) in a position close to the bolt body to bolt head transition. The structure is aged martensite.
55
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Brittle Fracture
ML00136 — Hydrogen Cracks of Subsea StudsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Fractographic aspect of the stud fracture surface, by scanning electron microscopy, close to the bottom of the thread fillet. In the center of the image it is possible to see secondary cracks with intergranular morphology.
59
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
ML00009 — Hydrogen Cracking of a 5" Drill Pipe S135M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Detail of the fracture surface with a starting point at the external surface of the pin.
91
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Brittle Fracture
Macroscopic detail of the fracture surface with a starting point at the external surface of the pin.
82
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Fracture Surface AspectDf - Brittle Fracture
ML00088 — Hydrogen Cracking of an API 5D S135 Drill PipeM - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Visual aspect of the tool joint (TJ) that fractured in the pin body when it was assembled (the box appears as a sleeve in the pin OD). The internal coating is not damaged. The fracture is flat and presents little evidences of plastic deformation, indicating that the pin broke in a brittle way.
69
VIEW
ML00088 / Dec.2017
Hydrogen Cracking of an API 5D S135 Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect by NDTDf - Brittle Fracture
Detail of the flat fracture surface of the pin, after disassembling from the TJ box. ID in the top and OD in the bottom of the figure. Radial marks are clear in the fracture surface.
57
VIEW
ML00088 / Dec.2017
Hydrogen Cracking of an API 5D S135 Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Fracture Surface AspectDf - Brittle Fracture
Fractographic analysis of the pin fracture surface showing inter and transgranular morphologies of fracture micromechanisms.
53
VIEW
ML00088 / Dec.2017
Hydrogen Cracking of an API 5D S135 Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
Fractographic analysis of the pin showing several secondary intergranular cracks (in the middle of the figure) and quasecleavage transgranular fracture mechanism.
45
VIEW
ML00088 / Dec.2017
Hydrogen Cracking of an API 5D S135 Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Surface Aspect by SEMDf - Brittle Fracture
ML00078 — Hydrogen Cracking of IN 718 Subsea ConnectorM - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Fractography by SEM, showing intergranular and transgranular fracture micromechanisms.
72
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
ML00076 — Hydrogen Cracking of a 17-7 PH Subsea SpringM - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
The low magnification fractography by SEM shows a brittle fracture of the spring wire, with several secondary cracks.
45
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
The fractography by SEM presents intergranular (in the previous austenite grain boundaries) and transgranular fracture micromechanisms. Several secondary cracks perpendicular to the fracture surface.
46
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture