Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Naked Eye or Stereoscope clear all

High Temperature — sub-branches

Carburization 2Creep 3Microstructural Evolution 1Overheating 1Scaling 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Macroscopic aspect after cutting longitudinally in two halfs, at the damaged area. The tube internal surface showed a red copper colour at the overheated region and the perforation is associated to longitudinal cracks.
104
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Longitudinal Section AspectDf - Internal Surface
Transverse section macrography of the plate where the degradation by thinning is worst, close to the original corners of the tube. The thinning is occurrring from the product reaction side (side A to the bottom of the figure). The macrography shows a reduction in the thickness from 2 mm (right side, sample 2) to almost zero (left side, sample 1).
86
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Transverse Section AspectDf - Thinning
The macrography of a longitudinal section shows that the tube did not present local thinning in any region, but the internal and external scales are evidenced. The external surface (OD) is to the top of the figure and the internal surface (ID) is to the bottom of the figure.
124
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - NItal Etched MacroDf - Longitudinal Section
The macrography of a transverse section of the new tube shows that there are shrinkage voids close to the internal surface, that is exposed to high temperature air. The tube is a 4" diameter and 1/4" thick.
62
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - Transverse Section AspectDf - Casting Structure
Aspect of the internal side of the fitting, at the longitudinal seam weld, and macrography of a transverse section showing the through wall cracks.
62
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Transverse Section
Macrography of the NEW TUBE, centrifugally cast, in the transverse section, presenting columnar grains close to the external surface.
50
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Kalling Etched MacroDf - Transverse Section

More from these cases

ML00180 — Local Melting of Copper Cooling TubesM - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Detail of the perforation point, internal view. Aligned perforations in the overheated region and interconnected longitudinal cracks.
94
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Longitudinal Section AspectDf - Leakage
Transverse section of the tube in a position of localized thinning.
60
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Transverse Section AspectDf - Localized Thinning
Transverse section of the tube in a position of wall perforation.
32
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Transverse Section AspectDf - Leakage
Local Melting of Copper Cooling Tubes
1
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Transverse Section AspectDf - Thinning
Local Melting of Copper Cooling Tubes
1
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Transverse Section AspectDf - Leakage
ML00160 — High Temperature Degradation of 310SSM - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Longitudinal section macrography of the plate where the degradation by thinning is reducing the thickness from 6mm to 4mm (sample 3). The thinning is occurrring from the product reaction side (side A to the bottom of the figure).
83
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Longitudinal Section AspectDf - Thinning
ML00097 — Cast SS Tube Removed From High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
The macrography of a transverse section of the tube removed from service after 6 months, with damage close to the internal tube surface. The tube is a 4" diameter and 1/4" thick.
41
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - Transverse Section AspectDf - Casting Structure
ML00038 — Cast SS Tube for High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Macrography of the TUBE REMOVED FROM SERVICE, centrifugally cast, in the transverse section, presenting thickness loss and macrostructure deterioration.
33
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Kalling Etched MacroDf - Transverse Section