Fatigue

1 case · 5 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Segregation Bands Capture method: NItal Etched Macro clear all

Fatigue — sub-branches

Fatigue Induced by a Defect 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography of the longitudinal section of the valve body, at the cracked position close to the actuator hole. The valve body is 40 mm thick and at this position it is possible to see that there are two regions where the body was welded, close to the inner surface (bottom) and at the close to the outer surface (top). The through wall crack presented a branch aspect close to the repair in the ID and a straight aspect when propagating from the repair.
55
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - NItal Etched MacroDf - Weld Repair

More from these cases

ML00162 — Valve Body Crack Growth from Weld DefectsM - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Macrographic detail of the cracked position close to the actuator hole. The through wall crack presented a branch aspect in the weld metal, that is the original defect created during welding, and a straight aspect when propagating from the repair.
27
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - NItal Etched MacroDf - Hot cracking
Macrographic detail of the longitudinal section of the valve body, at the cracked position, a little far from the actuator hole. There is a straight crack, transverse to the thickness that clearly propagated by fatigue mechanism, from the region where the welding defects were created.
27
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - NItal Etched MacroDf - Fatigue Crack
Valve Body Crack Growth from Weld Defects
2
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - NItal Etched MacroDf - Crack
Valve Body Crack Growth from Weld Defects
1
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - NItal Etched MacroDf - Fatigue Crack