Fabrication Defect

2 cases · 3 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Fracture Surface Aspect clear all

Fabrication Defect — sub-branches

Casting Defect 1Coating Defect 1Heat Treatment Defect 4Not according to spec 4Welding Defect 9

Results

SortNewestOldestTitle A-ZTitle Z-A
The fracture is flat, in the region of the lower resistant section, presenting no macroscopic evidences of plastic deformation. The starting point of the fracture is indicated by the chevron marks.
62
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Fracture Surface AspectDf - Chevron Marks
Aspect of the all weld metal broken tensile test conducted in the sample removed from structure close to the region where the cracking was detected, indicating that the material entrapped hydrogen for several days, since the test was conducted more than 2 weeks later than the cracking was detected.
61
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Fracture Surface AspectDf - Fish Eye

More from these cases

ML00148 — Brittle Fracture of a 420 SS Barrel NutM - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Macroscopically brittle fracture of the barrel nut, starting at the edge of the thread, as shown by the chevron marks.
29
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Fracture Surface AspectDf - Chevron Marks