Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Standard: A Detail focus: Damage clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
The threads of the carbon steel valve body is corroded. The offshore ambient is wet and chloride rich, creating an aggressive environment for the carbon steel threads.
99
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Surface AspectDf - Corrosion
Detail of the margin of the perforated hole in the impact position. It is interesting to observe that the perforation caused the material to be expulsed from the hole, in the direction of the impact.
39
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Surface AspectDf - Plastic Deformation
Nitronic 60 cylinder. Detailed aspect of the pitting in a low magnification microscope.
197
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Surface AspectDf - Pitting
Aspect of the butt welded joint surface, after grinding to remove the reinforcement, polishing and macro etching. There are multiple cracks, transverse to the weld and restricted to the weld metal. The surface hardness are 167HB for the tube (left side), 180 HB for the Forged T (right side) and 272 HB for the weld metal, suggesting lack of a suitable PWHT.
181
VIEW
ML00071 / Jan.2019
Reheating Cracking of a CrMo Vessel Weld
M - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
Cm - Surface AspectDf - Cracks

More from these cases

ML00184 — Dissimilar Steels in a Threaded ConnectionM - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Not only the threads were corroded but all regions under the painting that was detached from the surface.
86
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Surface AspectDf - Corrosion
ML00143 — Impact of a .308 Winchester on A36 PlateM - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Detail of the plate surface a little far from the perforated hole, in the side where the projectil stroke the plate. Drops of melted material from the bullet.
34
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Surface AspectDf - Melted film
ML00121 — Pitting Corrosion in a Subsea SystemM - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
17-4 PH rod. Detailed aspect of the pitting in a low magnification microscope.
115
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Surface AspectDf - Pitting