Scanning Electron Microscope

3 cases · 16 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: S32750 clear all

Scanning Electron Microscope — sub-branches

Electrolytic Etch Micrography by SEM 4Fractography by SEM 4Micrography by SEM 1Surface Aspect by SEM 7

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect by scanning electron microscopy of the cracking at the external surface of the fitting.
47
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - External Surface
Micrographic detail of the flange base metal presenting a coarse duplex ferritic austenitc structure and detrimental phases associated to the ferritic structure.
47
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - Electrolytic Etch Micrography by SEMDf - Duplex structure
External surface aspect of the flange showing preferential dissolution, responsible for nucleation of the through wall cracking.
245
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - Surface Aspect by SEMDf - Preferential Dissolution

More from these cases

ML00094 — MIC of a Subsea Hydraulic LineM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Aspect by scanning electron microscopy of the cracking at the external surface of the fitting. Interesting to observe that the cracks are deformed.
39
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - External Surface
Aspect by scanning electron microscopy of the cracking at the internal surface of the fitting.
36
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Internal Surface
Aspect by scanning electron microscopy of the cracking at the internal surface of the fitting. Interesting to observe multiple cracks with brittle characteristic.
39
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Internal Surface
The internal surface of the fitting presents multiple cracks not associated to pitting.
38
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Internal Surface
The through wall cracking was opened by citting the two sides and the aspect was characterized by SEM. Although there was a film at the fracture surface, probably because the fitting was removed from service some time after it was leaking, the fracture micromechanism is by quasecleavage, typical of a stress corrosion cracking.
56
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Fractography by SEMDf - Transgranular Fracture
ML00049 — Pipe to Flange Welded Joint in a 14" ND Superduplex SpoolM - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Micrographic detail of the flange base metal presenting a coarse duplex ferritic austenitc structure and detrimental phases associated to the ferritic structure.
39
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - Electrolytic Etch Micrography by SEMDf - Duplex structure
ML00002 — Preferential Dissolution and Cracks in SDSSM - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Detail of the region at the flange external surface where the material is suffering the preferential corrosion.
177
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - Surface Aspect by SEMDf - Preferential Dissolution
Micrographic detail of the through wall cracking in the middle of the thickness, showing that the cracking is associated to ferrite network in the (super)duplex microstructure.
128
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - Micrography by SEMDf - Crack
Micrographic detail of the cracking, associated to the ferrite network, that presents both corrosion (preferential dissolution) and fracture (clevage) aspects.
128
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - Electrolytic Etch Micrography by SEMDf - Crack
The fracture surface, although presenting a large amount of corrosion products, shows also evidences of a brittle behavior with regions of cleavage micromechanism.
116
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - Fractography by SEMDf - Cleavage Facets
Micrographic detail of the ferrite network with evidences of precipitation/formation of detrimental phases. NaOH solution was adopted for the electrolytic etching.
86
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - Electrolytic Etch Micrography by SEMDf - Delta ferrite

+2 more from this case →