Scanning Electron Microscope

1 case · 4 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: 718 clear all

Scanning Electron Microscope — sub-branches

Fractography by SEM 4

Results

SortNewestOldestTitle A-ZTitle Z-A
Transgranular brittle aspect of the stud fracture surface. Evidences of hydrogen embrittlement.
965
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Secondary Cracks

More from these cases

ML00075 — Hydrogen Cracking of IN 718 Subsea FastenersM - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
The secondary cracks are easily observed in the fracture surface, longitudinal to the axis of the stud.
26
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
The fracture of the stud presented both intergranular and transgranular aspects.
26
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
The fracture of the stud presented transgranular aspects and secondary cracks that appear to be related to small broken particles.
32
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Secondary Cracks