Scanning Electron Microscope

2 cases · 9 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Dendritic clear all

Scanning Electron Microscope — sub-branches

Electrolytic Etch Micrography by SEM 3Micrography by SEM 6

Results

SortNewestOldestTitle A-ZTitle Z-A
Image by scanning electron microscopy of the metallurgically bonded interface of the internally cladded pipe. It is a seamless pipe in a low alloy steel X70 cladded by welding overlay of Alloy 625 (by automatic GTAW process). The region is a detail of the interface inside the Ni alloy weld metal, presenting columnar grains and intragranular preciptation. The pipe was heat treated before bending (solution annealing) and after bending (quenching and tempering to meet X70 grade). The microhardness of this region is higher than the value obtained out of this region, in the overlay.
656
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Electrolytic Etch Micrography by SEMDf - Clad Interface
Low magnification micrography of the welded region, showing the interface between the base in the bottom and the fusion zone (between the liquidus and solidus temperatures), as well as the weld metal in the top. There are pores close to the weld metal and in the fusion zone the interdendritic space was melted and the eutectic morphology was changed. Keller etch.
50
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Weld Repair

More from these cases

ML00132 — Seamless Pipe Overlaid with Alloy 625M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Image by scanning electron microscopy of the interface of the internally cladded pipe. It is a seamless pipe in low alloy steel X70 overlaid with Alloy 625 (by automatic GTAW process). The region is a detail in the side of the Ni alloy weld metal, presenting transgranular precipitation. The pipe was heat treated before bending (solution annelaing) and after bending (quenching and tempering to meet X70 grade). The microhardness of this region is higher than the value obtained out of this region, in the overlay.
42
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Electrolytic Etch Micrography by SEMDf - Clad Interface
Image by scanning electron microscopy of the interface of the internally cladded pipe, seamless low alloy steel X70 overlaid with Alloy 625 (by automatic GTAW process) and presenting maximum iron content of 5% at the thickness of 3 mm (the qualified thickness).
36
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Electrolytic Etch Micrography by SEMDf - Clad Interface
ML00070 — Automotive Light Alloy Wheel Repaired By WeldingM - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Micrographic detail of the cast rim at the heat affected zone presenting coalesced Si particles at the interdendritic space an neddles of Fe rich phase. Keller etch.
47
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Heat Affected Zone
The coalesced silicon particles in the interdendritic space of the base metal presents a remelting at the fusion zone. The micrography by SEM shows the exactly line where the eutectic is remelted and refined. Keller etch.
40
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Fusion Line
Refined dendrites in the weld metal. The Si/Al alpha eutectic in the interdendritic space is also refined. Keller etch.
38
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Weld Metal
Hot cracks in the fusion zone. The eutectic regions were melted and cracked in an interdendritic morphology.
37
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Cracks
Detail of the hot cracks in the fusion zone. The eutectic regions were melted and cracked in an interdendritic morphology. Keller etch.
50
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Cracks