Scanning Electron Microscope

2 cases · 5 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Standard: ASME clear all

Scanning Electron Microscope — sub-branches

Fractography by SEM 5

Results

SortNewestOldestTitle A-ZTitle Z-A
Fractographic analysis by scanning electron microscopy of the stud fracture surface after opening the cracks. Brittle intergranular morphology with dimples and quasecleavage micromechanisms indicate that the internal cracks, intergranular, occurred by a hydrogen embrittlement effect during electroplating, and the ductile aspects are probably associated to overloading during torque.
517
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Fracture
The fracture surface of the main pipe is presented in low magnification (external pipe surface in the top) showing a flat propagation starting from the contour of the weld margin.
173
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Margin of the Weld Crack

More from these cases

ML00127 — Hydrogen Cracks of Cadmium Plated StudsM - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Fractographic analysis by scanning electron microscopy of the stud fracture surface after opening the cracks. Brittle intergranular morphology with dimples and quasecleavage micromechanisms indicate that the internal cracks, intergranuar, occurred by a hydrogen embrittlement effect during electroplating, and the ductile aspects are probably associated to overloading during torque.
37
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Intergranular Cracking
ML00006 — Vibration Induced Fatigue in 304SSM - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Fracture surface micromechanism by striation, evidence of FATIGUE.
158
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation
Fracture surface micromechanism by striation, evidence of FATIGUE.
147
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation