Scanning Electron Microscope

3 cases · 9 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Welded Joint Condition: Damage Microstructure: Austenite clear all

Scanning Electron Microscope — sub-branches

Fractography by SEM 3Surface Aspect by SEM 6

Results

SortNewestOldestTitle A-ZTitle Z-A
The fracture surface in the sample shows columnar grains in the weld and large facets in the heat affected zone (HAZ) close to the internal surface of the carcass (to the top of the image).
32
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Fractography by SEMDf - Brittle Fracture
Scanning electron microscopy image of the external surface of the line at the cracking position showing multiple cracks, branched, transverse to the line axis.
79
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - External Surface
Fracture surface after opening the shell cracking, presenting fatigue striation. The fracture presents also foreign particles.
132
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Fractography by SEMDf - Fatigue Striation

More from these cases

ML00174 — Carburization of a 347 SS Welded JointM - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Detail of the fracture in the heat affected zone, showing a flat fracture where the fracture is close to the surface of the plate, exposed to the high temperature exhausting gases.
24
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Fractography by SEMDf - Brittle Fracture
ML00095 — MIC of a Riser Control LineM - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Detail, by scanning electron microscopy, of the external surface of the line at the cracking position presenting branched cracks, transverse to the line axis. The surface of the fitting is fully stained (dark grey), from where the cracks start, indicating that the material loose passivation in these regions.
62
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Branched Cracks
The aspect of the fitting surface by SEM shows multiple cracks. Interesting to observe a stained region (dark grey) that corresponds to regions where the material passivation was destroyed.
43
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - External Surface
Detail of one region that had the passivation layer destroyed .
45
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - External Surface
Detail of one region that had the passivation layer destroyed and presented corrosion cracks.
48
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Corrosion Cracking
The aspect of the external surface of the fitting shows regions where the passivation was lost and where microcracks started already.
54
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Microcracks