Scanning Electron Microscope

2 cases · 11 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Corrosion Microstructure: Martensite clear all

Scanning Electron Microscope — sub-branches

Fractography by SEM 9Surface Aspect by SEM 2

Results

SortNewestOldestTitle A-ZTitle Z-A
The microscopic aspect of the internal side of the housing evidences the characteristics of the multiple cracks, not directly related to pitting corrosion.
41
VIEW
ML00093 / Sep.2017
MIC of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Cracks
Microscopic detail of the fracture surface in the position where the fracture is intergranular, probably due to the MIC attack creating an embrittled condition of the material.
31
VIEW
ML00080 / Sep.2017
MIC of Stacking Disc Springs
M - Low Alloy Medium Carbon QTP - SpringAp - SubseaCd - Brittle Behavior
Cm - Fractography by SEMDf - Intergranular Fracture

More from these cases

ML00093 — MIC of a Drilling ToolM - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Brittle Behavior
Details of the pitting corrosion at the internal surface. There are cracks inside some pits.
31
VIEW
ML00093 / Sep.2017
MIC of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Pitting
The fracture micromechanism is intergranular in the region where the failure has iniciated.
22
VIEW
ML00093 / Sep.2017
MIC of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Brittle Behavior
Cm - Fractography by SEMDf - Intergranular Fracture
Fractographic detail by SEM of the intergranular micromechanism in the region where the failure has iniciated.
25
VIEW
ML00093 / Sep.2017
MIC of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Brittle Behavior
Cm - Fractography by SEMDf - Intergranular Fracture
The fracture micromechanism is transgranular by quasecleavage in the region where the failure has propagated.
21
VIEW
ML00093 / Sep.2017
MIC of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Brittle Behavior
Cm - Fractography by SEMDf - Transgranular Fracture
Fractographic detail by SEM of the transgranular micromechanism by quasecleavage in the region where the failure has propagated.
21
VIEW
ML00093 / Sep.2017
MIC of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Brittle Behavior
Cm - Fractography by SEMDf - Transgranular Fracture
ML00080 — MIC of Stacking Disc SpringsM - Low Alloy Medium Carbon QTP - SpringAp - SubseaCd - Brittle Behavior
Microscopic detail of the fracture surface in the position where the fracture is intergranular, probably due to the MIC attack creating an embrittled condition of the material. A surface film is evident in this position suggesting that the fracture remained open and exposed to the environment during a certain time before the failure was detected.
29
VIEW
ML00080 / Sep.2017
MIC of Stacking Disc Springs
M - Low Alloy Medium Carbon QTP - SpringAp - SubseaCd - Brittle Behavior
Cm - Fractography by SEMDf - Intergranular Fracture
Fracture micromechanisms. Intergranular fracture in the top of the figure (close to the groove) and transgranular fracture in the bottom of the figure, where the mechanism changed to transgranular by quasecleavage.
27
VIEW
ML00080 / Sep.2017
MIC of Stacking Disc Springs
M - Low Alloy Medium Carbon QTP - SpringAp - SubseaCd - Brittle Behavior
Cm - Fractography by SEMDf - Intergranular Fracture
Microscopic detail of the fracture surface where it is transgranular, by quasecleavage. This aspect is similar to the one expected for this high strenght material without any embrittlement.
27
VIEW
ML00080 / Sep.2017
MIC of Stacking Disc Springs
M - Low Alloy Medium Carbon QTP - SpringAp - SubseaCd - Brittle Behavior
Cm - Fractography by SEMDf - Transgranular Fracture
Microscopic detail of the fracture surface where it is transgranular, by quasecleavage. This aspect is similar to the one expected for this high strenght material without any embrittlement.
26
VIEW
ML00080 / Sep.2017
MIC of Stacking Disc Springs
M - Low Alloy Medium Carbon QTP - SpringAp - SubseaCd - Brittle Behavior
Cm - Fractography by SEMDf - Transgranular Fracture