Scanning Electron Microscope

2 cases · 11 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Offshore Microstructure: Austenite clear all

Scanning Electron Microscope — sub-branches

Fractography by SEM 5Micrography by SEM 1Surface Aspect by SEM 5

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of a micrographic sample by scanning electron microscopy showing the external pipe surface, in the bottom, the fracture at the left side of the figure and several spots of pitting corrosion from the external surface. The polished section (transverse to the fracture and in a longitudinal section of the pipe) shows the morphology of the pit , 0.2 mm depth. Original magnification 50x.
54
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Micrography by SEMDf - Pitting
Regions of the pin thread presenting pitting corrosion.
635
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Surface Aspect by SEMDf - Localized Corrosion

More from these cases

ML00012 — Vibration Induced Fatigue in a 316/316L SSM - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Fracture aspect after opening the cracking, in the location where the fatigue cracking was iniciated. There is a pitting corrosion, 0.3 mm depth.
58
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Crack
Detail of the fatigue fracture iniciation point, at the surface, in a pitting corrosion 0.3 mm depth.
58
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Pitting
Fractographic detail of the pitting corrosion in the region of iniciation of the fatigue cracking, at the external surface of the pipe.
52
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Pitting
Detail of the fatigue fracture propagation, with striation micromechanism.
48
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation
Fractographic detail of fatigue striation.
41
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation

+2 more from this case →

ML00016 — SCC in Free Cutting 303SSM - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Regions of the localized corrosion spots associated to non metallic inclusions.
123
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Surface Aspect by SEMDf - Non Metallic Inclusions
Detail of the pin surface showing that the material easily cracks because it presents regions of localized corrosion.
45
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Surface Aspect by SEMDf - Fracture