Optical Microscope

13 cases · 36 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Bolt Detail focus: Microstructure clear all

Optical Microscope — sub-branches

Kalling Etched Micrography by OM 10Micrography by OM using A262 Method A 12Nital Etched Micrography by OM 12Oxalic Acid Electrolytic Etch 2

Results

SortNewestOldestTitle A-ZTitle Z-A
Metallographic detail of the longitudinal section of the clamp with a ferritic pearlitic structure.
32
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Low magnification micrography, by optical microscope, of the longitudinal section of a damaged bolt, in the center of the thickness. The microstructure is austenitic, free from carbides.
100
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Austenite
Micrographic detail of the rolled thread that was heat treated later. The bolt was quenched and tempered to 30 HRc and presented a martensitic structure.
110
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of a longitudinal section of the bolt in the center of the thickness, presenting a ferritic pearlitic structure with elongated grains due to the forming process, without later heat treatment.
173
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of a longitudinal section in the center of the bolt. Granular austenitic microstructure, equiaxial, primary precipitates (isolated), precipitation hardened (not detectable by metalography, only because of the hardness level)
431
VIEW
ML00106 / Dec.2017
Inconel 718 Submarine Bolt
M - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Austenite
Micrography of the bolt in a longitudinal section, at the bolt head, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
31
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Austenite
Micrographic detail of the strain hardened austenitic structure in the longitudinal section of the bolt.
441
VIEW
ML00101 / Nov.2017
High Strength 316SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Austenite
Micrographic detail of the strain hardened austenitic structure in the longitudinal section of the bolt.
412
VIEW
ML00087 / Nov.2017
High Strength Austenitic SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Austenite

More from these cases

ML00171 — Corrosion Fatigue of U Bolt Pipe ClampM - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Metallographic detail of the ferritic perlitic structure.
31
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
ML00157 — Bolts Under Chloride SCC ConditionsM - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Micrography, by optical microscope, of the longitudinal section of a damaged bolt, in the center of the thickness. The microstructure is austenitic, free from carbides, strain hardened. The hardness values of the material are from 200HV1 to 300HV1, that meets the class 2 of strenght (ASTM A193 B8M class 2).
79
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Strain Hardened
Detail of the strain hardened austenitic microstructure. Micrography by optical microscope, of the longitudinal section of a bolt, in the center of the thickness.
76
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Strain Hardened
ML00130 — Fatigue Fracture of Overloaded BoltsM - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
The microstructure of the bolt is martensitic in the center of the thickness. Longitudinal section.
103
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - Martensite
ML00120 — Ductile Rupture of a Carbon Steel Eye BoltM - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Micrographic detail of the ferritic pearlitic structure, with grains sligthly elongated.
157
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of a longitudinal section of the bolt at the bottom of the thread fillet, presenting a plastically deformed ferritic pearlitic structure. This analysis was conducted far from the failure and the structure was created by the cold forming process to manufacture the thread.
147
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - Nital Etched Micrography by OMDf - Strain Hardened
ML00105 — Inconel 718 Bolt of Special HeadM - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Micrographic detail of the bolt in a longitudinal section, at the bolt head, showing no evidences of forming operations, indicating it was machined from a heat treated bar. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
26
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Equiaxial Grains
Micrography of a longitudinal section in the center of the bolt. Austenitic microstructure, granular, equiaxial, precipitation hardened (shadow in the grains).
35
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Austenite
Micrographic detail of a longitudinal section in the center of the bolt. Granular austenitic microstructure, equiaxial, primary precipitates (isolated), precipitation hardened (shadow grains).
30
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Austenite
ML00101 — High Strength 316SS BoltM - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Micrography of the longitudinal section of the bolt, in the center of the body thickness. Strain hardened austenic structure.
52
VIEW
ML00101 / Nov.2017
High Strength 316SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Strain Hardened
Micrography of the longitudinal section of the bolt, in the center of the body thickness. Strain hardened austenic structure.
46
VIEW
ML00101 / Nov.2017
High Strength 316SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Strain Hardened
Micrography of the longitudinal section of the bolt, at the thread. The bolt was cold deformed and the thread was cold rolled.
32
VIEW
ML00101 / Nov.2017
High Strength 316SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Strain Hardened
Micrography of the longitudinal section of the bolt, at the thread. The bolt was cold deformed and the thread was cold rolled.
31
VIEW
ML00101 / Nov.2017
High Strength 316SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Strain Hardened
Micrographic detail of the strain hardened austenitic structure at the thread.
25
VIEW
ML00101 / Nov.2017
High Strength 316SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Austenite
ML00087 — High Strength Austenitic SS BoltM - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Micrography of the longitudinal section of the bolt, in the center of the body thickness. Strain hardened austenic structure.
73
VIEW
ML00087 / Nov.2017
High Strength Austenitic SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Strain Hardened
Micrography of the longitudinal section of the bolt, in the center of the body thickness. Strain hardened austenic structure.
62
VIEW
ML00087 / Nov.2017
High Strength Austenitic SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Strain Hardened
Micrography of the longitudinal section of the bolt, at the thread. The bolt was cold deformed and the thread was cold rolled.
65
VIEW
ML00087 / Nov.2017
High Strength Austenitic SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Strain Hardened
Micrography of the longitudinal section of the bolt, at the thread. The bolt was cold deformed and the thread was cold rolled.
65
VIEW
ML00087 / Nov.2017
High Strength Austenitic SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Strain Hardened
Micrographic detail of the strain hardened austenitic structure at the thread.
59
VIEW
ML00087 / Nov.2017
High Strength Austenitic SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Micrography by OM using A262 Method ADf - Austenite