Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Tube Condition: Used Standard: ASTM clear all

Optical Microscope — sub-branches

FeCl3+HCl+H2O Etched Micro 3Micrography by OM using A262 Method A 3Nital Etched Micrography by OM 20

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic structure. Pearlite colonies in bands.
401
VIEW
ML00116 / Jan.2018
CMn Steel Structural Tubing 6 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of a transverse section of the 5 mm thick tubing, in the center of the thickness. Ferritic-pearlitic structure, with the pearlite presenting a coalesced aspect. The tubing was in service at ambient temperature, painted, and the coalesced aspect was generated before service, perhaps during the tubing manufacturing.
393
VIEW
ML00115 / Jan.2018
CMn Steel Structural Tubing 5 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic structure. Pearlite colonies in bands.
346
VIEW
ML00114 / Jan.2018
CMn Steel Structural Tubing 8 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of a longitudinal section of the pipe showing that the carbon steel pipe is slightly banded and there is a decarburized layer at the solid solution welded interface. The stainless steel structure (in the right side of the figure) is not revealed using the Nital etch.
126
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
The micrography of the tube shows a granular structure and light deformation lines. No evidences of corrosion from the external surface (upper side of the figure) or internal surface (lower side of the figure).
440
VIEW
ML00043 / Apr.2017
CuNi Condenser Tube
M - CupronickelP - Seamless tubeAp - Heat ExchangerCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Longitudinal Section

More from these cases

ML00116 — CMn Steel Structural Tubing 6 mm thickM - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Low magnification micrography of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic banded structure.
30
VIEW
ML00116 / Jan.2018
CMn Steel Structural Tubing 6 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Banded Structure
Micrography of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic structure. Bands of pearlite colonies. Refined grains.
26
VIEW
ML00116 / Jan.2018
CMn Steel Structural Tubing 6 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of a transverse section of the tubing in the center of the thickness. Ferritic-pearlitic structure. The structure is fully ferritic in a small extension at the surface, due to a decarburization effect during manufacturing.
26
VIEW
ML00116 / Jan.2018
CMn Steel Structural Tubing 6 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrographic detail of a transverse section of the tubing, close to the internal surface. Ferritic-pearlitic structure, refined.
20
VIEW
ML00116 / Jan.2018
CMn Steel Structural Tubing 6 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
ML00115 — CMn Steel Structural Tubing 5 mm thickM - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Low magnification micrography of a transverse section of the tubing, in the center of the thickness. Banded structure, ferritic-pearlitic.
16
VIEW
ML00115 / Jan.2018
CMn Steel Structural Tubing 5 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Banded Structure
Micrography of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic structure. The pearlite is banded and presented a coalesced aspect.
12
VIEW
ML00115 / Jan.2018
CMn Steel Structural Tubing 5 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrographic detail of a transverse section of the tubing, at the external surface. Ferritic-pearlitic structure. The roughness of the surface is high because the structure was painted and a blasting treatment was probably applied to the surface to improve adherence.
15
VIEW
ML00115 / Jan.2018
CMn Steel Structural Tubing 5 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrographic detail of a transverse section of the tubing, close to the internal surface. Ferritic-pearlitic structure. Very close to the surface the amount of ferrite is higher than in the center and the grain is coarser, due to a decarburization effect probably occurred when the surface was exposed to high temperature during manufacturing.
13
VIEW
ML00115 / Jan.2018
CMn Steel Structural Tubing 5 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
ML00114 — CMn Steel Structural Tubing 8 mm thickM - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Low magnification micrography of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic banded structure.
29
VIEW
ML00114 / Jan.2018
CMn Steel Structural Tubing 8 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Banded Structure
Micrography of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic structure. Bands of pearlite colonies. Refined grains.
30
VIEW
ML00114 / Jan.2018
CMn Steel Structural Tubing 8 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of a transverse section of the tubing, at the external surface. Ferritic-pearlitic structure. The roughness of the surface is high because the structure was painted and a blasting treatment was probably applied to the surface to improve adherence.
20
VIEW
ML00114 / Jan.2018
CMn Steel Structural Tubing 8 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of a transverse section of the tubing, close to the internal surface. Ferritic-pearlitic structure, refined.
16
VIEW
ML00114 / Jan.2018
CMn Steel Structural Tubing 8 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
ML00056 — Seamless Tube Externally Cladded with SSM - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Micrography of a longitudinal section of the pipe showing the carbon steel pipe , internal.
123
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of a longitudinal section of the pipe showing the stainless steel pipe , external.
100
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Micrography by OM using A262 Method ADf - Austenite
Micrographic detail of the interface in the longitudinal section of the pipe showing the Vickers (300g) microhardness values, close to the interface in the carbon steel side and in the stainless steel side. Although the Nital etch does not allow to reveal the structure in the stainless steel side, the high hardness values show that the structure is different.
113
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrographic detail of the interface in the longitudinal section of the pipe showing the decarburized layer at the solid solution welded interface. The stainless steel structure (in the right side of the figure) is not revealed using the Nital etch.
80
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Clad Interface
Micrography of the interface between the carbon steel that is strongly etched by the electrolytic oxalic acid (in the left side of the figure) and the stainless steel, in the longitudinal section of the pipe. There is a strain hardened layer very close to the interface, at the stainless steel side.
79
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Micrography by OM using A262 Method ADf - Longitudinal Section

+2 more from this case →

ML00043 — CuNi Condenser TubeM - CupronickelP - Seamless tubeAp - Heat ExchangerCd - Removed From Service
The material structure is monophasic.
110
VIEW
ML00043 / Apr.2017
CuNi Condenser Tube
M - CupronickelP - Seamless tubeAp - Heat ExchangerCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Single phase
Detail of the structure at the surface.
79
VIEW
ML00043 / Apr.2017
CuNi Condenser Tube
M - CupronickelP - Seamless tubeAp - Heat ExchangerCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - At the Surface