Low magnification micrography of the nut in the longitudinal section, presenting the machined internal thread and a banded microstructure.
55
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Banded Structure
Micrography of the pin close to the interface with the spray and fuse layer. Transverse section. The fuse was conducted in high temperature and the pin was cooled very slowly, forming a ferritic-perlitic structure even for this high hardenability base metal.
35
VIEW
ML00110 / Jan.2018
Non Conformance in Spray and Fuse Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite

More from these cases

ML00148 — Brittle Fracture of a 420 SS Barrel NutM - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Microstructural aspect of a longitudinal section of the nut, in the middle of the thickness. Martensitic structure, banded.
46
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Banded Structure
Microstructural detail of the banded structure. The rough aspect of the band is created by the carbides (better seen in the higher magnification image) in the segregation band.
38
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Banded Structure
Micrographic detail of the nut longitudinal section presenting the large carbides (white islands) in the segregation band, and small precipitates all through the martensite matrix, indicating that this high carbon steel was tempered in a high temperature. The 36HRc hardness also confirms this high tempering temperature.
39
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Martensite
Vickers microhardness identations using 100 grams. In a position out of the band (top line). Values from left to right, 380HV; 390HV and 394HV. In a position inside the band (bottom line). Values from left to right, 433HV, 483HV and 473 HV.
33
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Banded Structure
Low magnification micrography of the nut in the longitudinal section, presenting the machined internal thread and a banded microstructure. It is possible to see that the contact pressure in the thread caused a surface plastically deformation.
24
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Banded Structure
ML00110 — Non Conformance in Spray and Fuse PinM - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Heat Treatment Defect
Micrography of the ferritic-pearlitic structure in the center of the thickness of the tubular forging pin. Transverse section. The fuse is conducted in high temperature and the pin was not heat treated after the thermal spray deposition and fuse.
23
VIEW
ML00110 / Jan.2018
Non Conformance in Spray and Fuse Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the ferritic-pearlitic structure in the center of the thickness of the tubular forging pin. Transverse section. The fuse is conducted in high temperature and the pin was not heat treated after the thermal spray deposition and fuse.
21
VIEW
ML00110 / Jan.2018
Non Conformance in Spray and Fuse Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite