Optical Microscope

11 cases · 24 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Raw Material Condition: Damage Detail focus: Ferrite and Pearlite clear all

Optical Microscope — sub-branches

Nital Etched Micrography by OM 24

Results

SortNewestOldestTitle A-ZTitle Z-A
The tube microstructure is ferritic-pearlitic, typical of this kind of material. No evidences of microstrutural changes were detected (no overheating, no decarburization).
177
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of the plate in a section, showing a ferritic-pearlitic microstructure in the middle of the thickness.
84
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of the longitudinal section of the cylinder, at the external diameter (right side of the figure), presenting smaller interdendritic graphite flakes in a ferritic-perlitic matrix. It is also possible to see free carbides (cementite) very close to the cylinder surface (less than 50 microns), associated to positions of graphite. This surface was painted.
25
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of the pipe transverse section presenting a predominatly ferritic-perlitic microstructure.
132
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic aspect of the longitudinal section of the cylinder steel substrate, presenting a ferritic-pearlitic structure.
207
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of the pin close to the interface with the spray and fuse layer. Transverse section. The fuse was conducted in high temperature and the pin was cooled very slowly, forming a ferritic-perlitic structure even for this high hardenability base metal.
35
VIEW
ML00110 / Jan.2018
Non Conformance in Spray and Fuse Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of a transverse section of the pipe, external diameter 26.7 mm, in the center of the 7.85mm thickness. Refined structure but not uniform. Ferrite and pearlite.
512
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of a longitudinal section of the tube, 200 mm far from the cracked region, in the center of the thickness (3.9 mm) showing a granular ferritic-perlitic structure.
139
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite

More from these cases

ML00143 — Impact of a .308 Winchester on A36 PlateM - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Micrography of the plate in a section, showing a ferritic-pearlitic microstructure in the middle of the thickness, in a position where the plate was not affected by the shot.
65
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the plate in a section, showing a ferritic-pearlitic microstructure in the middle of the thickness.
66
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the ferritic-pearlitic microstructure.
53
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
ML00140 — Preferential Corrosion of Pipe Seam WeldM - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Micrographic detail of the predominatly ferritic-perlitic microstructure. Pipe transverse section.
95
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
ML00128 — MIC of a Stored Hydraulic CylinderM - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Micrographic detail of the ferritic-pearlitic structure of the cylinder steel substrate.
41
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
ML00110 — Non Conformance in Spray and Fuse PinM - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Heat Treatment Defect
Micrography of the ferritic-pearlitic structure in the center of the thickness of the tubular forging pin. Transverse section. The fuse is conducted in high temperature and the pin was not heat treated after the thermal spray deposition and fuse.
23
VIEW
ML00110 / Jan.2018
Non Conformance in Spray and Fuse Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the ferritic-pearlitic structure in the center of the thickness of the tubular forging pin. Transverse section. The fuse is conducted in high temperature and the pin was not heat treated after the thermal spray deposition and fuse.
21
VIEW
ML00110 / Jan.2018
Non Conformance in Spray and Fuse Pin
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
ML00111 — 3/4" XXS Pipe Not Qualified for Low TempM - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Micrography of a transverse section of the pipe, close to the internal surface (ID). Refined structure. Ferrite and pearlite. The structure is not uniform. There is a large variation in the ferritic grain size and the pearlite colonies appear forming a network.
39
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of a transverse section of the pipe, close to the external surface (OD). Refined structure. Ferrite and pearlite. The structure is not uniform. There is a large variation in the ferritic grain size.
28
VIEW
ML00111 / Dec.2017
3/4" XXS Pipe Not Qualified for Low Temp
M - Low Carbon SteelP - Seamless PipeAp - RefineryCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
ML00104 — Thermal Fatigue of a Boiler TubeM - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Micrographic detail of a longitudinal section of the tube, 200 mm far from the cracked region, in the center of the thickness (3.9 mm). Feritic perlitic structure.
113
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of the longitudinal section of the tube, close to OD, showing no damage in a section about 200mm far from the cracked region.
92
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of the longitudinal section of the tube, close to ID, showing no damage in a section about 200mm far from the cracked region.
69
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite