Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Finished Product Condition: Brittle Behavior Detail focus: Cracking clear all

Optical Microscope — sub-branches

As polished micrography 1Micrography by OM 1Nital Etched Micrography by OM 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the cracking parallel to the fracture, as polished. The fracture is branched, there are several secondary cracks, with a clear intergranular morphology.
65
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - As polished micrographyDf - Cracking
Micrography as polished of the region where there was a refrigeration hole, presenting a cracking.
35
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - Micrography by OMDf - Cracking

More from these cases

ML00138 — Liquid Metal Embrittlement of a HSLA SteelM - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Micrography of the branch cracking parallel to the fracture. There are several secondary intergranular cracks and the cracks are filled with zinc. The zinc appears dark because of the Nital etch, and the steel is not fully revealed because of the protection by the zinc.
54
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Cracking