Optical Microscope

4 cases · 29 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Subsea Condition: Damage Microstructure: Austenite clear all

Optical Microscope — sub-branches

Kalling Etched Micrography by OM 15Micrography by OM using A262 Method A 14

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the case, observed in the center of the thickness, showing an equiaxial granular austenitic microstructure, free from carbides. The structure is typical of a 316 SS, in a solution annealed condition.
176
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Micrography by OM using A262 Method ADf - Austenite
Nitronic 60 cylinder. Micrography of the longitudinal section in the center of the thickness, presenting a fully austenitic microstructure, equiaxial grains, and evidences of the manufacturing process by hot forming.
179
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Micrography by OM using A262 Method ADf - Austenite
Micrography of the longitudinal section of the forging material, presenting a granular austenite, precipitation hardened.
84
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
The stud presents an austenitic structure, with primary and secondary precipitates of a size that is visible in low magnification microscopy.
55
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Austenite

More from these cases

ML00122 — Crevice Corrosion in a Subsea SystemM - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Micrographic detail of the fully austenitic granular structure of the case, in the center of the thickness.
158
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Micrography by OM using A262 Method ADf - Austenite
Microstructure of the welded region of the padeye, at the fusion line. The weld metal is dendritic, austeno ferritic, in the left side of the figure. The heat affected zone is in the center of the figure and shows no changes in relation to the base metal. The padeye base metal is to the right side of the figure.
120
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Micrography by OM using A262 Method ADf - Welded Joint
Micrographic detail of the fusion line of the welded joint of the padeye. The connector where the padeye was installed was welded to the case, but presented no evidences of corrosion.
110
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Micrography by OM using A262 Method ADf - Welded Joint
Micrographic detail of the crevice corrosion in the case wall, showing that the structure is not affected and is fully austenitic with equiaxial grains typical of a solution annealed condition.
85
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Micrography by OM using A262 Method ADf - Localized Corrosion
Micrographic detail of the crevice corrosion in the case wall, showing that the structure is not affected and is fully austenitic with equiaxial grains typical of a solution annealed condition.
72
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Micrography by OM using A262 Method ADf - Localized Corrosion

+2 more from this case →

ML00121 — Pitting Corrosion in a Subsea SystemM - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Nitronic 60 cylinder. Micrography of the longitudinal section in the center of the thickness, presenting a fully austenitic microstructure, with some aligned non metallic inclusions.
157
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Micrography by OM using A262 Method ADf - Austenite
Nitronic 60 cylinder. Micrographic detail of the longitudinal section in the center of the thickness, presenting a fully austenitic microstructure, equiaxial grains, typical of a solution annealed condition.
136
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Micrography by OM using A262 Method ADf - Austenite
Nitronic 60 cylinder. Micrography of the longitudinal section close to the surface, presenting a fully austenitic microstructure, with a shadow close to the external surface that is associated to a small layer of strain hardened structure (deformation twins).
133
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Micrography by OM using A262 Method ADf - Strain Hardened
Nitronic 60 cylinder. Micrography of the longitudinal section close to the surface, presenting a fully austenitic microstructure, with a 0.15mm layer of strain hardened structure (deformation twins).
120
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Micrography by OM using A262 Method ADf - Strain Hardened
Nitronic 60 cylinder. Micrographic detail of the longitudinal section close to the surface, presenting a fully austenitic microstructure, with a layer of strain hardened structure (deformation twins).
113
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Micrography by OM using A262 Method ADf - Strain Hardened

+4 more from this case →

ML00078 — Hydrogen Cracking of IN 718 Subsea ConnectorM - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Micrography of the longitudinal section of the conector, at the fracture position, showing secondary cracks from the fracture surface.
64
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Fracture
The micrographic detail of the longitudinal section at the fracture surface shows intergranular morphology for the secondary cracks (longitudinal to the forging axis).
64
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Secondary Cracks
Micrographic detail of a longitudinal section of the connector, at the fracture surface (in the top), showing intergranular secondary cracks.
54
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Intergranular Cracking
Micrographic detail of a longitudinal section of the connector, at the fracture surface (in the top), showing intergranular secondary cracks. There is a large amount of delta phase precipitated intergranular and intragranluar.
48
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Secondary Cracks
ML00075 — Hydrogen Cracking of IN 718 Subsea FastenersM - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
The stud structure evidences grain boundaries precipitation of probably delta phase (an overaging of the hardening precipitate).
49
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Austenite
Micrography of a longitudinal section of the stud, at the fracture surface, in the thread.
44
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Fracture
Micrographic detail of a longitudinal section of the stud, at the fracture surface, in the thread. It is possible to see primary precipitates (yellow) already cracked and intergranular propagation.
37
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Intergranular Cracking
Micrography of a longitudinal section of the stud, at the fracture surface in the center of the thickness, showing a long secondary cracking (vertical in the left).
35
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Secondary Cracks
Micrographic detail of the longitudinal section of the stud, at the secondary cracking.
27
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Brittle Cracks