Optical Microscope

4 cases · 12 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Structure Condition: Used Detail focus: Sampling and Analysis clear all

Optical Microscope — sub-branches

Nital Etched Micrography by OM 12

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic structure. Bands of pearlite colonies. Refined grains.
26
VIEW
ML00116 / Jan.2018
CMn Steel Structural Tubing 6 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic structure. The pearlite is banded and presented a coalesced aspect.
12
VIEW
ML00115 / Jan.2018
CMn Steel Structural Tubing 5 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of a transverse section of the tubing, in the center of the thickness. Ferritic-pearlitic structure. Bands of pearlite colonies. Refined grains.
30
VIEW
ML00114 / Jan.2018
CMn Steel Structural Tubing 8 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of the transverse section of the rolled shape presenting an aligned structure, ferritic-pearlitic. Transverse section.
97
VIEW
ML00035 / Dec.2017
Carbon Steel L Shape
M - Low Carbon SteelP - Rolled ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness

More from these cases

ML00116 — CMn Steel Structural Tubing 6 mm thickM - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Micrography of a transverse section of the tubing in the center of the thickness. Ferritic-pearlitic structure. The structure is fully ferritic in a small extension at the surface, due to a decarburization effect during manufacturing.
26
VIEW
ML00116 / Jan.2018
CMn Steel Structural Tubing 6 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrographic detail of a transverse section of the tubing, close to the internal surface. Ferritic-pearlitic structure, refined.
20
VIEW
ML00116 / Jan.2018
CMn Steel Structural Tubing 6 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
ML00115 — CMn Steel Structural Tubing 5 mm thickM - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Micrographic detail of a transverse section of the tubing, at the external surface. Ferritic-pearlitic structure. The roughness of the surface is high because the structure was painted and a blasting treatment was probably applied to the surface to improve adherence.
15
VIEW
ML00115 / Jan.2018
CMn Steel Structural Tubing 5 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrographic detail of a transverse section of the tubing, close to the internal surface. Ferritic-pearlitic structure. Very close to the surface the amount of ferrite is higher than in the center and the grain is coarser, due to a decarburization effect probably occurred when the surface was exposed to high temperature during manufacturing.
13
VIEW
ML00115 / Jan.2018
CMn Steel Structural Tubing 5 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
ML00114 — CMn Steel Structural Tubing 8 mm thickM - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Micrography of a transverse section of the tubing, at the external surface. Ferritic-pearlitic structure. The roughness of the surface is high because the structure was painted and a blasting treatment was probably applied to the surface to improve adherence.
20
VIEW
ML00114 / Jan.2018
CMn Steel Structural Tubing 8 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the External Surface
Micrography of a transverse section of the tubing, close to the internal surface. Ferritic-pearlitic structure, refined.
16
VIEW
ML00114 / Jan.2018
CMn Steel Structural Tubing 8 mm thick
M - CMn SteelP - Seamless Round ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
ML00035 — Carbon Steel L ShapeM - Low Carbon SteelP - Rolled ShapeAp - StructureCd - Removed From Service
Micrography of the transverse section of the rolled shape presenting a ferritic-pearlitic microstructure. Transverse section, close to the surface.
80
VIEW
ML00035 / Dec.2017
Carbon Steel L Shape
M - Low Carbon SteelP - Rolled ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - At the Surface
Micrography of the transverse section of the rolled shape presenting an aligned structure, ferritic-pearlitic.
62
VIEW
ML00035 / Dec.2017
Carbon Steel L Shape
M - Low Carbon SteelP - Rolled ShapeAp - StructureCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Transverse Section