Optical Microscope

3 cases · 4 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Ship Detail focus: Transgranular Cracking clear all

Optical Microscope — sub-branches

Nital Etched Micrography by OM 4

Results

SortNewestOldestTitle A-ZTitle Z-A
Metallographic aspect of the cracks showing that several microcracks join from different pits and growth through the section, in a transgranular morphologyy.
26
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Transgranular Cracking
Micrographic detail of the crack at the edge of the tube. This is not the best direction of analysis because the cracks are parallel to the analyzed section. It is possible to see the crack from the surface, large and filled with oxides.
75
VIEW
ML00119 / Feb.2018
Thermal Fatigue of a Marine Boiler
M - Low Carbon SteelP - Fabrication WeldAp - ShipCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Transgranular Cracking
Micrographic detail of a cracking with inclusions decohesion at the bottom of the thread.
51
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Transgranular Cracking

More from these cases

ML00171 — Corrosion Fatigue of U Bolt Pipe ClampM - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Metallographic aspect of one secondary cracking, paralell to the fracture surface, growthing with an irregular path and transgranular morphologyy.
28
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Transgranular Cracking