Optical Microscope

3 cases · 4 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: O&G Well Drilling Detail focus: Cracking clear all

Optical Microscope — sub-branches

Nital Etched Micrography by OM 4

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of the through wall cracking, slightly branched and thin.
656
VIEW
ML00093 / Sep.2017
MIC of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Brittle Behavior
Cm - Nital Etched Micrography by OMDf - Cracking
Micrography of a longitudinal section of the pin, at the fracture position, showing a low magnification aspect of the fracture surface (top of the figure) and secondary cracks associated to the segregation band.
51
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Cracking
Micrography of the welded joint fusion line presenting the liquation cracking. The weld metal is in the right side (bottom) and the forged connector heat affected zone is in the left side (top).
83
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracking

More from these cases

ML00093 — MIC of a Drilling ToolM - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Brittle Behavior
A micrography of the housing in a transverse section showing a through wall cracking, slightly branched and thin. The internal surface of the housing appears in the bottom of the figure.
26
VIEW
ML00093 / Sep.2017
MIC of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Brittle Behavior
Cm - Nital Etched Micrography by OMDf - Cracking