Nital Etched Micrography by OM

12 cases · 32 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: Heat Affected Zone clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Fusion line of the forging side, in the cap, showing the weld metal (to the top of the image) and the base metal (to the bottom of the image). The heat affected zone hardness is about 270HV10.
108
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
HAZ SURFACE
72
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Last Bead HAZ
Micrography presenting the coarse grain heat affected zone of the welded joint, at the cap pass. The microstructure is bainitic.
82
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrographic detail of the microstructure close to the corroded area showing the heat affected zone of the autogenous weld, with a refined grain size. The hardness level here is 202HV average, compared to the base metal that is 180HV average.
37
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the heat affected zone at the face of the joint. It is possible to see that even close to the fusion line the material was reheated in high temperature, suggesting that the temper bead was effective.
53
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Low magnification micrography of the tube HAZ, at the fusion line. The weld metal is in the right side of the figure and the tube weld metal is in the left side of the figure.
112
VIEW
ML00119 / Feb.2018
Thermal Fatigue of a Marine Boiler
M - Low Carbon SteelP - Fabrication WeldAp - ShipCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Low magnification micrography of a longitudinal section of a 4 mm diameter wire, at the region where the pearlitic strain hardened wire is affected by the welding. The base metal is to the left side and the region of the HAZ that starts with a grain growth is to the right side.
24
VIEW
ML00113 / Jan.2018
Autogenous Weld of a Carbon Steel Wire
M - Medium Carbon SteelP - WireAp - OffshoreCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the tubular 4130 forging at the heat affected zone (HAZ) of the Inconel overlay (white because it was not etched with the Nital). The structure is ferritic/bainitic because the overlay was conducted in two layers, and all the HAZ was reheated during welding.
66
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone

More from these cases

ML00177 — Cr-Mo Seam Welded TubeM - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
HAZ SURFACE
66
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Last Bead HAZ
HAZ T/2
33
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
HAZ T/2
35
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
HAZ ROOT
27
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Root HAZ
HAZ ROOT
27
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Root HAZ
ML00129 — Non qualified WPS for High Strength SteelM - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Micrography of the heat affected zone at the face of the joint, close to the fusion line. The hardness level at the HAZ was 248 HV10.
58
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the heat affected zone at the root of the joint, submitted to several welding reheating cycles.
36
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the heat affected zone at the root of the joint, submitted to several welding reheating cycles. The structure is still martensitic but presented a refined previous austenite structure.
30
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
ML00113 — Autogenous Weld of a Carbon Steel WireM - Medium Carbon SteelP - WireAp - OffshoreCd - Welding
Micrography of a longitudinal section of a 4 mm diameter wire, at the heat affected zone created by the autogenous welding, presenting a tempered martensitic structure.
19
VIEW
ML00113 / Jan.2018
Autogenous Weld of a Carbon Steel Wire
M - Medium Carbon SteelP - WireAp - OffshoreCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
ML00102 — AISI 4130 Forging Welded and OverlaidM - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Micrography of the tubular 4130 forging at the heat affected zone (HAZ) of the Inconel overlay (white because it was not etched with the Nital). The structure is ferritic/bainitic because the overlay was conducted in two layers, and all the HAZ was reheated during welding.
61
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the tubular 4130 forging at the heat affected zone (HAZ), butt weld face. The structure is tempered martensite because the welded joint was PWHT at 630°C. The original forging was normalized and tempered at 660°C.
49
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the tubular 4130 forging at the heat affected zone (HAZ) at the face of the butt weld. The structure is a tempered martensite because the joint was PWHT at 630°C. The original forging was normalized and tempered at 660°C.
43
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the tubular 4130 forging at the heat affected zone (HAZ), butt weld root. The structure is ferritic bainitic because of the multiple reheatings in high temperature.
51
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the tubular 4130 forging at the heat affected zone (HAZ), butt weld root. The structure is ferritic bainitic because of the multiple reheatings in high temperature.
34
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone