Naked Eye or Stereoscope

8 cases · 10 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Welding clear all

Naked Eye or Stereoscope — sub-branches

Electrolytically Etched Macro 3Kalling Etched Macro 2NItal Etched Macro 4NaOH Electrolytic Etched Macro 1

Results

SortNewestOldestTitle A-ZTitle Z-A
The macrography of a longitudinal section shows the low alloy (C-Mn) steel pipe, internally cladded with Ni alloy clad plate.
72
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Electrolytically Etched MacroDf - Longitudinal Section
The macrography of a longitudinal section shows the low alloy (C-Mn) steel pipe, internally cladded by overlay in two layers.
88
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Electrolytically Etched MacroDf - Longitudinal Section
Macrography of a longitudinal section of a 4 mm diameter wire, presenting part of an austogenously welded joint, with the transformation of the strain hardened pearlitic. The base metal is to the left side of the figure, and the heat affected zone is in the center of the figure. There is a (previous austenite) grain growth to the right side of the figure, where it is the center of the weld.
33
VIEW
ML00113 / Jan.2018
Autogenous Weld of a Carbon Steel Wire
M - Medium Carbon SteelP - WireAp - OffshoreCd - Welding
Cm - NItal Etched MacroDf - Welded Joint
Macrography of the tubular forging, butt welded using a LAS filler metal, and overlaid using Inconel 625 filler metal. The micrographic characterization was conducted for the HAZ of the overlay and for the HAZ of the butt weld, at the root position (with several welding cycles) and at the face.
608
VIEW
ML00102 / May.2018
AISI 4130 Forging Welded and Overlaid
M - Low Alloy SteelP - CladdingAp - Oil and GasCd - Welding
Cm - Electrolytically Etched MacroDf - Welded Joint
Macrography of the welded joint between a forging connector (right side) and a seamless tubing (left side). It was welded in two passes by GTAW process.
168
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MacroDf - Welded Joint
Transversal section of the 625 nickel alloy multipass weld. Pipe of 1 1/4' thickness
71
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - NItal Etched MacroDf - Welded Joint
Macrosection transverse to the longitudinal seam weld, presenting the two passes, the first welded from the internal side and the second welded from the external side. It is possible to see the columnar grains of the weld and the heat affected zone (HAZ) from each pass. See the schematic drawing in the next figure
427
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - NItal Etched MacroDf - Welded Joint
Macrography of the welded joint upper part. Transverse section showing the different zones studied in this ML. See the schematic drawing in the next image.
454
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched MacroDf - Welded Joint

More from these cases

ML00053 — SAW Longitudinal Seam of X70 PipeM - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Micrography of the fusion line of the second pass (not reheated). The HAZ is bainitic and the weld metal presents columnar grains (of the previous austenite).
60
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - NItal Etched MacroDf - Fusion Line
ML00045 — Subsea Tubular F6NM Martensitic SSM - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Macrography of the welded joint, at the root position, presenting the different zones studied in this ML. Transverse section. See the schematic drawing in the next image.
47
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched MacroDf - Welded Joint