NItal Etched Macro

6 cases · 8 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Tempered Martensite Standard: UNS clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography of a stud longitudinal sectiion at the fracture position (top of the figure). It is possible to see a large secondary crack at the bottom of the thread fillet adjacent to the fracture surface, without any deformation evidence. This reveals a brittle material behavior, although the hardness measured at the stud end revealed 33HRc, as should be expected by the material specification.
56
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - NItal Etched MacroDf - Secondary Cracks
Macrography of the welded joint taken from the vertical up part of the joint, presenting the root in one pass, the fill of the joint in three passes, the cap in three passes and two temper bead passes. The 10" diameter tube, 9.5mm thick, was welded by GTAW in the root (80SD2 filler metal) and by SMAW for fill, cap and temper bead passes (10018-D2 filler metal).
79
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - NItal Etched MacroDf - Welded Joint
Macrography of a longitudinal section of the stud, showing the flat fracture of brittle aspect.
46
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - NItal Etched MacroDf - Longitudinal Section
Macrography of a "longitudinal" section of the padeye showing casting defects close to the internal diamater and a secondary crack, paralel to fracture, starting from the internal diameter. The fracture is not presented in this macro, it is to the top of the photo.
17
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - NItal Etched MacroDf - Cracking
Transversal section of the 625 nickel alloy multipass weld. Pipe of 1 1/4' thickness
72
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - NItal Etched MacroDf - Welded Joint
The macrography of a longitudinal section of the pipe and connector, at the welded joint, shows that the welding was conducted from both side of the groove, starting from the ID and finishing from the OD, ID later machined flush. The cracking was detected by ultrasonic test and the macro shows that it is at the fusion line, growthing into the weld metal. See the schematic drawing in the next figure
535
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - NItal Etched MacroDf - Longitudinal Section

More from these cases

ML00098 — Brittle Fracture of a Casting Lifting DeviceM - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Macrographic detail of the secondary crack, paralel to fracture, starting from the internal diameter of the padeye. The dendritic structure is evident.
13
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - NItal Etched MacroDf - Secondary Cracks
ML00072 — Liquation Cracks in a High Strength JointM - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Hot cracking at the fusion line of the connector side, in a welded joint between a forging and a pipe, in a macrographic sample. The region of the heat affected zone of the connector presents a dendritic aspect suggesting that the forging reduction rate of the connector was not too high and did not broke the cast structure.
110
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint