NItal Etched Macro

6 cases · 15 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: O&G Well Drilling clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography of the welded joint between the forging and the pipe, showing it was welded in a narrow gap, indicating by the arrow the location of the crack at the margin of the weld, in the forging side.
129
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint
Macrography of the longitudinal section of the valve body, at the cracked position close to the actuator hole. The valve body is 40 mm thick and at this position it is possible to see that there are two regions where the body was welded, close to the inner surface (bottom) and at the close to the outer surface (top). The through wall crack presented a branch aspect close to the repair in the ID and a straight aspect when propagating from the repair.
55
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - NItal Etched MacroDf - Weld Repair
Macrography of a longitudinal section of the pipe at the fracture position, in the thicker thickness. The external side of the pipe (OD) is to the rigth side of the figure, and the internal side of the pipe is to the left of the figure. There are several secondary cracks, opened to the OD, created during bending.
37
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - NItal Etched MacroDf - Plastic Deformation
A macrography of the housing in a transverse section showing a through wall cracking. The external side of the housing is in the top of the figure.
26
VIEW
ML00093 / Sep.2017
MIC of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Brittle Behavior
Cm - NItal Etched MacroDf - Transverse Section
The macrography of a longitudinal section of the pipe and connector, at the welded joint, shows that the welding was conducted from both side of the groove, starting from the ID and finishing from the OD, ID later machined flush. The cracking was detected by ultrasonic test and the macro shows that it is at the fusion line, growthing into the weld metal. See the schematic drawing in the next figure
535
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - NItal Etched MacroDf - Longitudinal Section
The longitudinal section of the 1/2" thick pipe close to the washout position shows that the external tool marks are like notches that are corroded and cracks are iniciating from the corroded regions. The top of the figure presents the external pipe surface and the bottom of the figure presents the internal pipe surface, with a green coating and the rusted washout.
154
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - NItal Etched MacroDf - Longitudinal Section

More from these cases

ML00162 — Valve Body Crack Growth from Weld DefectsM - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Macrographic detail of the cracked position close to the actuator hole. The through wall crack presented a branch aspect in the weld metal, that is the original defect created during welding, and a straight aspect when propagating from the repair.
27
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - NItal Etched MacroDf - Hot cracking
Macrographic detail of the longitudinal section of the valve body, at the cracked position, a little far from the actuator hole. There is a straight crack, transverse to the thickness that clearly propagated by fatigue mechanism, from the region where the welding defects were created.
27
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - NItal Etched MacroDf - Fatigue Crack
Valve Body Crack Growth from Weld Defects
2
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - NItal Etched MacroDf - Crack
Valve Body Crack Growth from Weld Defects
1
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - NItal Etched MacroDf - Fatigue Crack
ML00159 — Collapse of a Drill PipeM - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Macrography of a longitudinal section of the pipe at the fracture position, in the thinner thickness. The external side of the pipe (OD) is to the left side of the figure, and the internal side of the pipe is to the rigth of the figure. The fracture occurred by shearing the pipe in a single event (probably due to tensile stresses during removal).
37
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - NItal Etched MacroDf - Ductile Fracture
Macrographic detail of the longitudinal section of the pipe at the fracture position, in the thicker thickness. The several secondary cracks, opened to the OD, were created during bending and shows evidences of compression, responsible for the increase in the pipe thickness.
33
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - NItal Etched MacroDf - Ductile Fracture
Macrographic detail of a longitudinal section of the pipe at the fracture position, in the thinner thickness. The external side of the pipe (OD) is to the left in the figure, and the internal side of the pipe is to the rigth in the figure. The fracture occurred by shearing the pipe in a single event (probably due to tensile stresses during removal).
24
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - NItal Etched MacroDf - Ductile Fracture
ML00072 — Liquation Cracks in a High Strength JointM - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Hot cracking at the fusion line of the connector side, in a welded joint between a forging and a pipe, in a macrographic sample. The region of the heat affected zone of the connector presents a dendritic aspect suggesting that the forging reduction rate of the connector was not too high and did not broke the cast structure.
110
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint
ML00068 — Corrosion Fatigue of a 5" Drill PipeM - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Macrography of the longitudinal section of the pipe presenting multiple cracks from the tool marks.
122
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - NItal Etched MacroDf - Cracks Transverse to the Surface