Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: A clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
The dye check image shows the detected crack, 50 mm long, at the margin of the weld in the forging side.
137
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect by NDTDf - Cracking
After removal of the cracked part of the fitting, the dye check test indicated the presence of several cracks in the internal diameter (ID), out of the buttered layer, that means, in the fitting base metal.
42
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Aspect by NDTDf - Cracks
Aspect by dye check of the upper side of the pipe, at the margin of the weld between the main pipe and the lateral branch, presenting a fatigue cracking initiated at the external side, probably induced by vibration.
68
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect by NDTDf - Cracking
Aspect of the cracking after Dye Check Test (Liquid Penetrant) in the external side of the line that operates at 800°C, insulated, and presented the leakage associated to the longitudinal seam weld of the fitting. The circumferential butt weld of the fitting to a pipe did not fail. See the schematic drawing in the next figure
371
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Aspect by NDTDf - Through Wall Cracking
Image of the magnetic particle test, using a white contrast, presenting the cracks at the surface of the weld metal. The cracks are transverse to the weld and do not propagate into the base metals. A forged T in the right side of the figure and a thick wall tube in the left side of the figure, both in P12 CrMo steel.
1044
VIEW
ML00071 / Jan.2019
Reheating Cracking of a CrMo Vessel Weld
M - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
Cm - Aspect by NDTDf - Cracks
Aspect of the drum shell after removing the tubes and macroetching, indicating that the cracks were located in repair welded regions.
342
VIEW
ML00020 / Apr.2017
Intergranular SCC in Boiler Steam Drum Repair
M - Low Carbon SteelP - Repair WeldAp - BoilerCd - Stress Corrosion
Cm - Aspect by NDTDf - Cracks
The repair weld presented several cracks in the weld metal, transverse to the weld, detected during inspection using magnetic particle test. The cracks were mainly located in regions of the structure where the repair was conducted by welding in the vertical position using 1/8" stick electrode.
710
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Aspect by NDTDf - Cracking
Visual aspect of the repair welded plate surface, cracked during welding. Several cracks paralell to the welded regions, revealed by dye check, appear adjacent to the repair beads. The width of the repair is 15 mm.
153
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Aspect by NDTDf - At the Surface

More from these cases

ML00149 — Vibration Induced Fatigue in a Gas PipingM - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Aspect by dye check of the internal side of the 8" pipe, at the hole of the 2" lateral branch line, presenting the through thickness cracking initiated by fatigue at the external side, probably induced by vibration.
57
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect by NDTDf - Through Wall Cracking
Aspect by dye check of the upper side of the pipe, external, at the weld between the 8" main pipe and the 2" lateral branch, presenting a fatigue cracking initiated at the weld margin and propagating into the base metal in a longitudinal direction.
55
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect by NDTDf - Cracks
ML00010 — Cold Cracks in a Gouged Weld MetalM - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
After grinding to remove the cracks, it was possible to see that they originated in the root, with longitudinal and transverse cracking, and localized in the weld metal only.
167
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Aspect by NDTDf - Cracking