Aspect Before Analysis

13 cases · 38 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Martensite clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the broken disc spring, 1/4" thick, OD 10". The fracture is flat and transverse to the disc.
604
VIEW
ML00080 / Sep.2017
MIC of Stacking Disc Springs
M - Low Alloy Medium Carbon QTP - SpringAp - SubseaCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Brittle Fracture
Aspect of the fracture that occurred in the connection between the pin of one DP and the box of other DP, in the pin side. The photo presents the pin still connected in the box. The flat fracture indicates a brittle behavior.
641
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Aspect of the fillet weld between the superior plate (Low carbon 8 mm thick) and the inferior plate (C-Mn 12 mm thick), in an overlap geometry. In this region the welded joint was sound.
90
VIEW
ML00067 / May.2017
Cold Cracks in C-Mn SAW Weld Metal
M - CMn SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Aspect Before AnalysisDf - Welded Joint
Aspect of the washout in the 5" drill pipe, in the pipe body, before cleaning the surface.
683
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - At the Surface
Macroscopic aspect of the cutting surface, slightly irregular. The structural plate is 1 1/4" thick.
48
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Aspect Before AnalysisDf - At the Surface

More from these cases

ML00009 — Hydrogen Cracking of a 5" Drill Pipe S135M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Aspect of the broken pin after removal from the box end.
125
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Brittle Fracture
Detail of the fracture surface with a starting point at the external surface of the pin.
91
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Brittle Fracture
ML00067 — Cold Cracks in C-Mn SAW Weld MetalM - CMn SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Aspect of the fracture in the middle of the fillet weld between the superior plate (Low carbon 8 mm thick no longer there) and the inferior plate (C-Mn 12 mm thick), in an overlap geometry.
77
VIEW
ML00067 / May.2017
Cold Cracks in C-Mn SAW Weld Metal
M - CMn SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Aspect Before AnalysisDf - Fracture
ML00033 — Plasma Cut of 1 1/4" Steel PlateM - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Aspect of the 1 1/4" thickness plate cutting surface.
30
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Aspect Before AnalysisDf - At the Surface