Aspect Before Analysis

5 cases · 11 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Aged Martensite clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
General aspect of the 5/8" allen bolt that was found fractured in an instrument connected to a subsea BOP. The fracture presented a brittle aspect and occurred at the bolt head to threaded body transition.
1495
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Fracture
Aspect of the broken spring. The wire is 1 1/2" diameter and the ourter diameter of the spirals is 12 1/2", in a 20" height spring. It was broken in several pieces.
866
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - General View
Aspect of the Nitronic 60 cylinder, OD 36.4mm, presenting pits at the external surface.
219
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Aspect Before AnalysisDf - External Surface
The stainless steel spring broke without any evidence of plastic deformation. The round wire 1/8" diameter has ruptured in a brittle way in this 2" long spring of external diameter of 1/2".
73
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Aspect of the broken bolt 1 1/2" nominal diameter, after a short time in service (non residente subsea equipment) under cathodic protection. The bolt broke at the thread fillet, close to the head.
800
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00137 — Brittle Fracture of a 15-5 PH Valve SpringM - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Aspect of the fracture of the spring. Close to the surface the fracture presents the aspect of rusted spots.
132
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Fracture
The spring ruptured in several positions. This is the aspect of one of the fractures of the spring. In the initiation of the fracture (top side of the figure) the fracture presents a different morphology.
101
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Brittle Fracture
Corroded spots (shallow pits) at the spring surface.
84
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - At the Surface
Aspect of the fracture surface showing a strong difference between the fracture initiation and fracture propagation. This fracture was sectioned and the micrographies are presented showing the diferences in the fracture morphology.
40
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Fracture
ML00121 — Pitting Corrosion in a Subsea SystemM - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Aspect of the 17-4 PH rod, OD 10.6 mm, presenting deep pits at the external surface.
125
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Aspect Before AnalysisDf - External Surface
ML00076 — Hydrogen Cracking of a 17-7 PH Subsea SpringM - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Detailed aspect of the spring close to the fracture position. The wire surface shows a morphology that reveals the material structure.
58
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Fracture