Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Zinc Layer Detail focus: Fracture clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the other side of the fracture of the 2" diameter lifting device. It failed in a brittle way during loading test. The zinc coating was partially removed from the casting surface of one side of the failed part, for inspection, looking for casting defects. The results showed that the casting part did not present casting defects.
92
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Aspect Before AnalysisDf - Fracture