Aspect Before Analysis

4 cases · 8 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: 5D Detail focus: Damage clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Pipe fracture, flat, at the region of subcritical crack growth.
68
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fatigue Fracture
Macroscopic view of the fracture in the pipe body. In the bottom of the figure, the fracture of the pipe shows a thicker thickness, revealing that this is the pipe region that was first damaged by bending (buckling). In the top of the figure, the fracture shows a (ductile) shearing mechanism and the thickness is thinner, as will be better observed in the macrography.
39
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - Fracture
Aspect of the broken pin after removal from the box end.
125
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Brittle Fracture
Aspect of the fracture surface of the pin, still assembled in the box (that is externally to the pin). The pin fracture is flat, presenting radial marks.
791
VIEW
ML00088 / Dec.2017
Hydrogen Cracking of an API 5D S135 Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Brittle Fracture

More from these cases

ML00169 — Drill Pipe Fracture in the Pipe BodyM - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Fracture appearance in the side that was not damaged by the fishing, showing the two aspects of the fracture propagation, half by fatigue and half by shearing overloading.
48
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
Fracture appearance showing the two aspects of the fracture propagation, flat by fatigue and at 45 degrees by overloading.
35
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
Region of the pipe fracture, where there is a transition from the flat fatigue to the rough overloading.
27
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
ML00009 — Hydrogen Cracking of a 5" Drill Pipe S135M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Detail of the fracture surface with a starting point at the external surface of the pin.
91
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Brittle Fracture