Structure

3 cases · 19 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Microstructure: Strain Hardened Capture method: Aspect Before Analysis clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Concrete steel strand general view, presenting fracture of several wires and a corroded aspect. The full part is composed by 19 strands, each strand using 7 wires, and each wire about 5 mm diameter.
834
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Red painted device where the 50 mm x 50 mm 6061 T6 aluminum alloy plate was positioned (in the circle). The image presents the target, positioned 100 meters far from the gun, after the shot and the projectile perforated the plate.
478
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View
Red painted device where the 50 mm x 50 mm carbon steel plate was positioned (in the circle). The image presents the target, positioned 100 meters far from the gun, after the shot and the projectile perforated the plate, as will be presented in the other figures.
602
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00155 — Failure of a Prestressed Concrete Steel StrandM - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
General aspect of the degradated wires of the strand, most part presenting rust and rupture.
107
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
General aspect of the degradated wires of the strand, most part presenting rust and rupture. There are two mais aspects of the degradation: wire thickness reduction by corrosion and cracks creating a longitudinal fracture of several wires.
96
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
Macro view of individual strand wires emerging from the anchorage fitting, most surfaces covered in reddish-brown corrosion product and several wire ends showing fracture.
4
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Corrosion
Cross-section at the wire surface showing a deep corrosion pit with branching attack adjacent to the longitudinally drawn metal texture.
4
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Corrosion
Cross-sectional view of a wire showing irregular corrosion pits penetrating inward from both surfaces.
4
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Corrosion

+5 more from this case →

ML00145 — Impact of a .380 Winchester on 6061 T6 PlateM - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Aspect of the 3/8" thickness plate, 50 mm x 50 mm, of the aluminum alloy plate, in the face of impact with the projectile. The plate was perforated by the bullet.
52
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View
Other view of the 3/8" thickness, 50 mm x 50 mm, 6061 T6 aluminum plate, in the face of impact with the projectile. The plate suffered a localized perforation.
34
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View
Other view of the 3/8" thickness, 50 mm x 50 mm, 6061 T6 aluminum plate, in the opposite face of impact. The plate suffered a localized perforation and this image shows the position of the exit of the bullet.
30
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View
ML00143 — Impact of a .308 Winchester on A36 PlateM - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Aspect of the 3/8" thickness plate, 50 mm x 50 mm, of the low carbon steel steel, in the face of impact with the projectile. The plate was perforated by the bullet.
88
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View
Other view of the 3/8" thickness plate, 50 mm x 50 mm, of the low carbon steel plate, in the face of impact with the projectile. The plate suffered a localized perforation.
48
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View
Other view of the 3/8" thickness plate, 50 mm x 50 mm, of the low carbon steel plate, in the opposite face of impact. The plate suffered a localized perforation and this image shows the position of the exit of the bullet. It is also evident that the shot was very close to the red painted device since a straight line is marked at the surface of the plate (bottom of the figure).
46
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Aspect Before AnalysisDf - General View