Ship

2 cases · 14 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Welded Joint Detail focus: Welded Joint clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Summary of the welding conditions and qualification test results. NON QUALIFIED WPS. The individual parameters for each welding position are presented in the legend of each macrography, that also presents the amount of beads.
117
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - WPS summaryDf - Welded Joint
Macrography of the plate (thickness 22mm, in horizontal position) to tube (thickness 12.5 mm, in vertical position) welded joint. The half V groove was welded from the top (position inside the combustion chamber) in five weld beads, and with a small fillet welded from the water side (ouside of the tube). Average hardness of the plate is 180HV1 (1kg), of the tube is 150HV1 and of the weld is 190HV1. Maximum hardness of the tube HAZ is 165HV1 and plate HAZ is 195HV1.
219
VIEW
ML00119 / Feb.2018
Thermal Fatigue of a Marine Boiler
M - Low Carbon SteelP - Fabrication WeldAp - ShipCd - Thermal Fatigue
Cm - NItal Etched MacroDf - Welded Joint

More from these cases

ML00118 — Non qualified GMAW of Aluminum PlatesM - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Macrography of the flat position welded joint. It was welded in three passes, with the following parameters. Root pass - 157A, 21V, 146mm/s (wire speed), 3.2 mm/s (welding speed), 1090 J/mm. Second pass - 161A, 21V, 146mm/s (wire speed), 4.2 mm/s (welding speed), 833 J/mm. Third pass - 155A, 21V, 146mm/s (wire speed), 5.1 mm/s (welding speed), 664 J/mm.
48
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched MacroDf - Flat Position
Macrographic detail of the flat position welded joint, showing the three passes. The large extension of the heat affected zone in the root reveals the too high imposed energy, melting out of the root gap. The shining spots are pores.
42
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched MacroDf - Flat Position
Macrography of the horizontal position joint. It was welded in three passes, and one additional pass from the root. Root pass - 153A, 20V, 156mm/s (wire speed), 3.5 mm/s (welding speed), 933 J/mm. Second pass - 162A, 20V, 156mm/s (wire speed), 5.8 mm/s (welding speed), 592 J/mm. Third pass - 155A, 19V, 156mm/s (wire speed), 5.9 mm/s (welding speed), 523 J/mm. Additional at the root - 161A, 23V, 187mm/s (wire speed), 8.5mm/s (welding speed), 467J/mm.
47
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched MacroDf - Horizontal Position
Macrographic detail of the horizontal position welded joint, showing the three passes welded from one side and the fourth pass welded after removing the ceramic backing. Big pores and liquation were identified.
40
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched MacroDf - Horizontal Position
Macrography of the vertical up position welded joint. It was welded in three passes, with the following parameters. Root pass - 115A, 21V, 162mm/s (wire speed), 2.6 mm/s (welding speed), 1090 J/mm. Second pass - 143A, 21V, 162mm/s (wire speed), 5.5 mm/s (welding speed), 594 J/mm. Third pass - 144A, 21V, 162mm/s (wire speed), 6.1 mm/s (welding speed), 979 J/mm.
39
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched MacroDf - Vertical Up Position

+7 more from this case →