Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Corrosion Microstructure: Alpha clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect "as received" of the seamless tube at the curved position, showing the longitudinal crack and corrosion products at the tube surface.
836
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00165 — SCC of Aluminum Bronze Heating CoilM - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Aspect of the external tube surface after cleaning. It is possible to see that the cracks are longitudinal to the tube and localized in positions where the surface is corroded.
132
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - Surface AspectDf - External Surface
Aspect of the internal tube surface after a longitudinal cut, without cleaning. It is possible to see a clean surface inside the tube.
104
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - Surface AspectDf - Internal Surface
Micrography of the tranverse section of the tube, in the center of the thickness. There are small grains and large grains, characterizing a dual grain size. The large grains size is about 100 microns, more than 10 times larger than the average size of the smaller grains size.
101
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - FeCl3+HCl+H2O Etched MicroDf - Dual grain sizes
Micrographic detail of the alpha microstructure presenting dual grain sizes. Two different types of twins are presented in the structure: annealing twins and deformation twins, suggesting that the material was probably partially recristalized after cold deformation and stress relief treatment.
87
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - FeCl3+HCl+H2O Etched MicroDf - Alpha
Micrography of a transverse section of the bent tube, external surface (OD) to the top and internal surface (ID) to the bottom of the figure. At the through wall cracking position, the external surface presented a layer of intergranular corrosion.
95
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - As polished micrographyDf - Cracking

+12 more from this case →