Ship

3 cases · 6 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Surface Aspect Detail focus: Damage clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Detail of a sound teeth, showing marks of plastic deformation across the tooth surface.
53
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Surface AspectDf - Plastic Deformation
Aspect of the tubesheet after removal of the cooper alloy tubes and water cleaning. The corrosion is more intense in the regions of tube connection.
176
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - Surface AspectDf - Corrosion
Higher magnification macrography (in a stereoscope) of the surface exposed to the combustion chamber, presenting multiple cracks perpendicular to the internal diamater of the tube (left side of the figure). The cracks are located in the tube and propagated into the tube wall and welded joint.
75
VIEW
ML00119 / Feb.2018
Thermal Fatigue of a Marine Boiler
M - Low Carbon SteelP - Fabrication WeldAp - ShipCd - Thermal Fatigue
Cm - Surface AspectDf - Thermal Fatigue Cracks

More from these cases

ML00181 — Wear of a Carburized Hypoid GearM - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Macroscopic detail of the pitting damage and plastic deformation at the surface of non-fractured tooth.
58
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Surface AspectDf - Pitting
Macroscopic detail of the fractured tooth, showing marks of plastic deformation at the tooth surface and several longitudinal cracks in the contact surfaces.
46
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Surface AspectDf - Crack
Macroscopic detail of the fractured tooth, showing several longitudinal cracks in the contact surfaces, suggesting the occurrence of spalling damage.
44
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Surface AspectDf - Fatigue Crack