Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Aligned particles Capture method: Optical Microscope Detail focus: Welding Defect clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the welded joint, at the root, presenting hot cracks. The imposed high energy in the root due to the ceramic backing support created a condition for cracking.
1100
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Hot cracking

More from these cases

ML00118 — Non qualified GMAW of Aluminum PlatesM - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Micrography of the welded joint, at the root, showing hot cracks with intergranular morphology.
146
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Hot cracking
Micrographic detail of the welded joint, at the root, presenting hot cracks. The presence of these defects were responsible for reducing the material strenght (rupturing in lower strenght than the requirements) and ductility (cracking in bending tests).
116
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Hot cracking