Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: FeCl3+HCl+Ethanol Etched Micro clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a transverse section of the platesheet presenting a duplex structure, alpha (light yellow) and beta (orange) phases.
214
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - FeCl3+HCl+Ethanol Etched MicroDf - Alpha and Beta

More from these cases

ML00125 — Dezincification of a Cooler TubesheetM - BrassP - PlateAp - ShipCd - Preferential Dissolution
Same region of the previous figure, after etching. Micrography presenting the interface between the layer where the dezincification occurred (top of the figure) and the region where the material was not yet corroded (bottom of the figure, now etched to reveal the microstructure).
85
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - FeCl3+HCl+Etanol Etched MicroDf - Dezincification
Micrography of the interface between the layer where the dezincification occurred (top of the figure) and the region where the material was not yet corroded (bottom of the figure, etched to reveal the microstructure).It is clear that the cracks (black opened regions in the upper side of the figure) are associated to the red islands that correspond to the regions of beta phase (orange islands in the bottom of the figure),
103
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - FeCl3+HCl+Etanol Etched MicroDf - Dezincification
Micrography of the non corroded region of the tubesheet presenting a microstructure of alpha (light yellow phase) and beta (orange phase).
99
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - FeCl3+HCl+Etanol Etched MicroDf - Alpha and Beta
Micrographic detail of the non corroded region of the tubesheet presenting a microstructure of alpha (light yellow phase) and beta (orange phase).
77
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - FeCl3+HCl+Etanol Etched MicroDf - Alpha and Beta
Micrography of the corroded region of the tubesheet presenting a microstructure of alpha (light yellow ), but no longer beta. In the position of the beta phase it is possible to see the cooper rich island (light red) and cracks (black) due to the selective removal of the zinc.
75
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - FeCl3+HCl+Etanol Etched MicroDf - Dezincification

+1 more from this case →