Ship

3 cases · 14 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Ferritic pearlitic Capture method: Aspect Before Analysis clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect before cleaning of the heavy U bolt pipe clamp, 38 mm diameter wire, at the fractured position. It is possible to see that it broke in a region where the clamp was no longer coated and there is no insert in the groove (at the internal clamp diameter). The fracture is transverse to the clamp axis.
522
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Aspect of the 4" pipe that was in seawater service for 8 years and leaked in a longitudinal line that corresponds to the seam weld. The internal surface presented thick deposits. Although the pipe was cut with a thermal process, the analysis was conducted after mechanical cutting.
100
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - General View
Bimetallic engine bearing, removed from service at the end of its life.
356
VIEW
ML00083 / Oct.2017
Steel Back of a Bimetallic Engine Bearing
M - Low Carbon SteelP - Cold FormedAp - ShipCd - Removed From Service
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00171 — Corrosion Fatigue of U Bolt Pipe ClampM - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Aspect of the U bolt clamp with partial detachment of the coating (white brown) in a region where the polimeric insert (dirty white) is still in the wire groove at the internal clamp diameter (ID).
91
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Detailed aspect of the fractured position, in a region where the clamp was no longer coated and there is no insert in the groove (at the internal clamp diameter). The fracture is transverse to the clamp axis.
86
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
Same aspect of the previous image after cleaning, showing a subcritical propagation aspect (fatigue), starting at the groove (ID) and also at the clamp surface in the OD.
75
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
In the region where the polimeric insert was loose, the protective coating of the clamp has suffered detachment.
69
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Layer Detachment
Close to the ID of the clamp, at the groove position, there are cracks in the coating (white brown) and also at the substrate.
63
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Cracks

+3 more from this case →

ML00140 — Preferential Corrosion of Pipe Seam WeldM - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Aspect of the internal surface of the pipe after cutting, showing the colors of the internal deposits and the leaking line associated to the pipe seam.
288
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - Leakage
Aspect of the internal surface of the pipe after cleaning, showing the leakage line.
67
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - Internal Surface
Detailed aspect of the internal surface of the pipe after cleaning, in a region where the pipe was leaking.
62
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - Leakage