Ship

3 cases · 4 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Ferritic pearlitic Capture method: Aspect Before Analysis Detail focus: General View clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect before cleaning of the heavy U bolt pipe clamp, 38 mm diameter wire, at the fractured position. It is possible to see that it broke in a region where the clamp was no longer coated and there is no insert in the groove (at the internal clamp diameter). The fracture is transverse to the clamp axis.
522
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Aspect of the 4" pipe that was in seawater service for 8 years and leaked in a longitudinal line that corresponds to the seam weld. The internal surface presented thick deposits. Although the pipe was cut with a thermal process, the analysis was conducted after mechanical cutting.
100
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - General View
Bimetallic engine bearing, removed from service at the end of its life.
356
VIEW
ML00083 / Oct.2017
Steel Back of a Bimetallic Engine Bearing
M - Low Carbon SteelP - Cold FormedAp - ShipCd - Removed From Service
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00171 — Corrosion Fatigue of U Bolt Pipe ClampM - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Aspect of the U bolt clamp with partial detachment of the coating (white brown) in a region where the polimeric insert (dirty white) is still in the wire groove at the internal clamp diameter (ID).
91
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View