Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Tempered Martensite Capture method: Scanning Electron Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Microscopic image by scanning electron microscope (SEM) of the ring surface that presented pites under fouling deposits.
522
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Pitting
Detail of the pin fracture surface, presenting both a flat aspect and a rough aspect in a shearing section of 2.5 mm width.
727
VIEW
ML00046 / Jan.2018
Brittle Fracture of SS Shear Pin
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Intergranular Cracking
Cm - Fractography by SEMDf - Fracture

More from these cases

ML00124 — MIC of a Martensitic Valve RingM - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Microscopic details of the ring surface showing the fouling at the surface and localized corrosion under the deposits.
42
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Pitting
Higher magnification of the localized corrosion, showing that there are cracks at the margin of the corroded region.
39
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Pitting
SEM image showing a branching surface crack extending from a region of granular corrosion deposits into the polished substrate.
32
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Pitting
Intergranular morphology inside the pitting and evidences of chemical attack (dissolution).
36
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Pitting
ML00046 — Brittle Fracture of SS Shear PinM - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Intergranular Cracking
Fracture appearance in a sheared region, presenting a ductile morphology for the fracture micromechanism.
109
VIEW
ML00046 / Jan.2018
Brittle Fracture of SS Shear Pin
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Intergranular Cracking
Cm - Fractography by SEMDf - Ductile Fracture
Fracture appearance in a brittle region, presenting an intergranular morphology.
93
VIEW
ML00046 / Jan.2018
Brittle Fracture of SS Shear Pin
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Intergranular Cracking
Cm - Fractography by SEMDf - Intergranular Cracking