Automotive

3 cases · 6 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: Soundness clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrographic detail of the hardened layer, about 3mm deep from the surface. Important to observe that the bearing is not heat treated in the radius, only in the contact area. The hardness at the surface is 430HV and the hardness in the base metal is 260HV.
100
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - NItal Etched MacroDf - Surface Layer
Micrography of a longitudinal section of the bolt at the bottom of the thread fillet, presenting a plastically deformed ferritic pearlitic structure in a very small extension from the surface (about 0.1mm). This analysis was conducted in a position far from the failure and the structure was created by the cold forming process to manufacture the thread.
152
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - Nital Etched Micrography by OMDf - Rolled Thread
Transverse section of the 1/16" thick tube at the autogenous seam weld.
588
VIEW
ML00026 / Feb.2017
Autogenous Seam Welded Tube in Ferritic SS
M - Ferritic Stainless SteelP - Fabrication WeldAp - AutomotiveCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Autogenous Weld

More from these cases

ML00154 — High Strength Cast Iron CrankshaftM - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Micrography of the shaft below the heat treated surface, in the middle of the hardened layer. There is a gradient in the colours. Hardened surface in the top of the figure and nucleous in the bottom.
49
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - Nital Etched Micrography by OMDf - Surface Layer
Micrography of the shaft below the heat treated surface, close to the limit of the hardened layer. There is a gradient in the colours. Hardened surface in the top of the figure and nucleous in the bottom.
45
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - Nital Etched Micrography by OMDf - Surface Layer
ML00026 — Autogenous Seam Welded Tube in Ferritic SSM - Ferritic Stainless SteelP - Fabrication WeldAp - AutomotiveCd - Typical manufacturing
Seam welded tube, nominal diameter 2 1/4" and thickness 1/16".
106
VIEW
ML00026 / Feb.2017
Autogenous Seam Welded Tube in Ferritic SS
M - Ferritic Stainless SteelP - Fabrication WeldAp - AutomotiveCd - Typical manufacturing
Cm - Aspect Before AnalysisDf - Autogenous Weld