Microstructure
Retained Austenite
that remains untransformed within a 's after cooling, in a matrix that would otherwise be expected to be fully martensitic or another lower-temperature phase. Its presence affects hardness, dimensional stability, and toughness, making it an important quantity to identify when examining hardened .