Atlas

2 cases · 15 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Fine Transgranular Precipitation clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
The scanning electron microscopy image of the internal surface of the tube in position 2 shows a localized corrosion region with intergranular morphology, as well a crack from the corroded region.
1237
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Surface Aspect by SEMDf - Intergranular Corrosion
Transverse section of the blade showing large grains of this poliycristaline cast material.
421
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - H2SO4+HNO3+H3PO4 Etched MicroDf - Coarse Structure

More from these cases

ML00086 — Intergranular Corrosion of Sensitized 304SSM - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Micrography of the 1.65 mm thickness tube, in the middle of the thickness of the longitudinal section. This part of the tube is located in the colder part of the equipment, position 1. The material presented carbide precipitation at grain boundaries (not yet fully surrounding the grains) and at this point the tube presented no internal corrosion.
338
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Austenite
Micrography of the 1.65 mm thickness tube, in the middle of the thickness of the longitudinal section. This part of the tube is located in position 2, where the temperature was higher and the carbide precipitation increased during service.
272
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Precipitation
Micrography of the 1.65 mm thickness tube, in the middle of the thickness of the longitudinal section. This part of the tube is located in position 3, where intergranular and transgranular carbide precipitation occurred during service.
234
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intragranular Secondary Precipitation
The low magnification image of the internal surface of the tube, in position 2, shows several points of localized corrosion, with intergranular morphology.
193
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Surface Aspect by SEMDf - Intergranular Corrosion
Micrography of a longitudinal section of the tube in position 2, presenting thinning by intergranular corrosion at the internal surface.
193
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Corrosion

+3 more from this case →

ML00042 — Gas Turbine Blade IN 939, CoatedM - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Micrography of the blade, view inside the grain. The intragranular precipitation presents one unique size of precipitation, not yet coalesced, although the blade was in high temperature service for 50.000 hours. Etched by H2SO4 + HNO3 + H3PO4 reagent.
66
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - Micrography by SEMDf - Intragranular Secondary Precipitation
Micrography close to the surface of the blade, showing the diffusion coating (aluminum base alloy) that is still sound. No strong oxidation or erosion was detected.
53
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - H2SO4+HNO3+H3PO4 Etched MicroDf - Coating
Micrographic detail of the diffusion coating. H2SO4 + HNO3 + H3PO4 etched.
47
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - Micrography by SEMDf - Coating
Micrography as polished of the region where there was a refrigeration hole, presenting a cracking.
35
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - Micrography by OMDf - Cracking
The cracking from the refrigeration hole presents an intergranular morphology, as shown in the micrography of a transverse section of the blade.
35
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - H2SO4+HNO3+H3PO4 Etched MicroDf - Intergranular Cracking