“fatigue”

4 cases · 34 images for “fatigue”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Austenite Standard: ASTM clear all

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
Micrographic detail of the fatigue cracking at the margin of the flange to shell fillet weld.
485
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Micrography by OM using A262 Method ADf - Fatigue Crack
Macroscopic aspect of the 1" shaft fracture surface, revealing beach marks at the surface typical of fatigue, initiated from the surface of the spline shaft at the gear position.
498
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Fatigue Fracture
The main pipe, ND 18", has suffered a pipe through wall cracking at the margin of the 1 1/2" branch socket weld.
664
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Crack
After opening the crack the fracture surface presented different aspects close to the internal surface, in the initiation, and through the wall propagation. Detail of the transgranular striation, showing the contribution of pulsing loads.
98
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Fractography by SEMDf - Fatigue Striation

More from these cases

ML00050 — Fatigue Failure of a 316SS Pressure StabilizerM - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Aspect of the equipment presenting a through wall cracking at the margin of the fillet weld.
143
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Aspect Before AnalysisDf - Cracking
Macrography of the welded joint between the flange and the shell, indicating the position where the cracking was detected, at 90°.
117
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Welded Joint
The shell plate micrography showed an austenitic structure.
101
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Micrography by OM using A262 Method ADf - Austenite
The macrography of a transverse section of the shell to flange weld (Lepto's etch) shows that the cracking occurred through the shell plate thickness, at the margin of the fillet weld.
93
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Transverse Section AspectDf - Cracking
Fracture surface after opening the shell cracking, presenting fatigue striation. The fracture presents also foreign particles.
132
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Fractography by SEMDf - Fatigue Striation

+3 more from this case →

ML00041 — Fatigue Fracture of Inconel 718 Spline ShaftM - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
xx
117
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - At the Surface
Macroscopic aspect of the 1" shaft fracture surface, revealing beach marks at the surface typical of fatigue, initiated from the surface of the spline shaft at the gear position.
121
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Fatigue Fracture
SEM fractograph at 1200x magnification showing an intergranular fracture surface with angular, faceted grains and fine feather-like markings.
86
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Fracture
Microscopic detail of the transgranular striation in the fracture surface.
78
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Fracture
The micrography of a transverse section of the shaft shows the granular austenitic structure close to the surface of the shaft.
67
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Kalling Etched Micrography by OMDf - At the Surface

+7 more from this case →

ML00006 — Vibration Induced Fatigue in 304SSM - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
The macro section transverse to the welded region, show that the through wall cracking occurred in the pipe base metal, from the margin of the weld.
191
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Through Wall Cracking
Macro transverse to the weld showing that the fracture occurred in the main pipe, at the margin of the weld.
163
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Fracture
The fracture surface of the main pipe is presented in low magnification (external pipe surface in the top) showing a flat propagation starting from the contour of the weld margin.
173
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Margin of the Weld Crack
Fracture surface micromechanism by striation, evidence of FATIGUE.
158
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation
Fracture surface micromechanism by striation, evidence of FATIGUE.
147
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation

+4 more from this case →

ML00011 — Intergranular SCC of Pure NickelM - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
After opening the crack the fracture surface presented different aspects close to the internal surface, in the initiation, and through the wall propagation. Detail of the transgranular striation, showing the contribution of pulsing loads.
82
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Fractography by SEMDf - Fatigue Striation