Atlas

2 cases · 4 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Ferritic Detail focus: Welded Joint clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Gas piping. Aspect of a branching line 2" ND, lateral to a horizontal main pipe ND 8", welded using a weldolet. In the lower part of the branch there are no cracks.
61
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Welded Joint
Macrography of the welded joint taken from the vertical up part of the joint, presenting the root in one pass, the fill of the joint in three passes, the cap in three passes and two temper bead passes. The 10" diameter tube, 9.5mm thick, was welded by GTAW in the root (80SD2 filler metal) and by SMAW for fill, cap and temper bead passes (10018-D2 filler metal).
78
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - NItal Etched MacroDf - Welded Joint

More from these cases

ML00149 — Vibration Induced Fatigue in a Gas PipingM - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Macrography of a transverse section of the 8" pipe, cut exactly in the middle of the lateral 2" branch line, showing the through thickness crack initiated at the margin of the weld, in the upper part of the pipe.
64
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - NItal Etched MacroDf - Welded Joint
ML00129 — Non qualified WPS for High Strength SteelM - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
WPS welded in 6G qualification welding position and tested according to ASME IX and NACE ISO 15156. Minimum preheating of 250°C. Two temper bead passes. PWHT at 640°C during 12 hours. Tube diameter 10". Thickness 3/8". V groove 70°. Root opening 1/8". NOT APPROVED due to ULTIMATE STRENGHT lower than the base metal minimum requirements.
87
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - WPS summaryDf - Welded Joint