Atlas

2 cases · 3 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Austeno ferritic Detail focus: Through Wall Cracking clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the cracking after Dye Check Test (Liquid Penetrant) in the external side of the line that operates at 800°C, insulated, and presented the leakage associated to the longitudinal seam weld of the fitting. The circumferential butt weld of the fitting to a pipe did not fail. See the schematic drawing in the next figure
371
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Aspect by NDTDf - Through Wall Cracking
The macro section transverse to the welded region, show that the through wall cracking occurred in the pipe base metal, from the margin of the weld.
191
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Through Wall Cracking

More from these cases

ML00061 — Creep in a Seam Weld of a 304H SS FittingM - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Schematic drawing presenting the aspect of the cracking after Dye Check Test (Liquid Penetrant) in the external side of the line that operates at 800°C, insulated, and presented the leakage associated to the longitudinal seam weld of the fitting. The circumferential butt weld of the fitting to a pipe did not fail.
62
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Identification drawingDf - Through Wall Cracking