“fatigue”

2 cases · 8 images for “fatigue”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Martensite and Retained Austenite Detail focus: Microstructure clear all

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
Micrography of the pin microstructure at the longitudinal section showing a tempered martensitic structure and a band of retained austenite.
61
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Kalling Etched Micrography by OMDf - Martensite
Low magnification micrography of a longitudinal section of the valve body, in the center of the thickness. As expected for this high strength steel, the microstructure is martensitic, but with segregation bands.
48
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Banded Structure

More from these cases

ML00085 — Corrosion Fatigue of a Martensitic SS PinM - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Micrographic detail of the pin microstructure at the longitudinal section showing a tempered martensitic structure and a band of retained austenite.
62
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Kalling Etched Micrography by OMDf - Banded Structure
Micrographic detail of the pin microstructure at the longitudinal section showing a band of retained austenite in martensitic structure.
58
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Kalling Etched Micrography by OMDf - Martensite
ML00162 — Valve Body Crack Growth from Weld DefectsM - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Micrography of a longitudinal section of the valve body presenting a martensitic microstructure. The structure is banded and the darker regions show inclusions (grey sulfides).
50
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the martensitic microstructure, in the longitudinal section. The hardness of the valve body is 34 HRc (Rockwell C) all through the thickness.
47
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the weld repair at the fusion line. Weld metal to the right and heat affected zone to the left.
37
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Fusion Line
Micrographic detail of the fusion line.
33
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Fusion Line