Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: AISI Detail focus: Coarse Structure clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Microstructure of the heat affected zone (weld metal to the left side), exposed to high temperature exhausting gases. Large austenitic grain size and intergranular cracks fully opened and filled with oxides.
21
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Coarse Structure
Micrography of the wheel in the center of the thickness, presenting a predominantly pearlitic structure and average hardness abot 196HB.
74
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Coarse Structure
The coarse structure in the center of the shaft thickness is evidenced by free ferrite islands at the previous austenite grains. The presence of a pearlitic structure evidences the slow cool of the material.
85
VIEW
ML00152 / Dec.2018
Low Alloy Steel Pump Shaft
M - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Coarse Structure
Micrographic detail of the weld metal with islands of a coarse ferritic structure, degradated (recristalized) from an acicular morphology during to the long heat treatment cycle in high temperature. The post welding heat treatment (PWHT) was conducted during 12 hours at 640°C.
700
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Coarse Structure

More from these cases

ML00152 — Low Alloy Steel Pump ShaftM - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
The longitudinal section of the shaft, at the surface, presenting only a small refining in the previous austenite grain boundaries than in the center, indicating that the material was slowed colled from forming and not heat treated.
67
VIEW
ML00152 / Dec.2018
Low Alloy Steel Pump Shaft
M - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Coarse Structure