Atlas

2 cases · 8 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Removed From Service Detail focus: Weld Metal clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
The weld metal presents the same structure than the base metal (alpha aluminum dendrites with Si/Al alpha eutectic in the interdendritic space) but refined when compared to the base metal. Also the hardness level is higher for the weld metal than the base metal.
37
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Weld Metal
Micrography of the weld metal with columnar grains and reheated and refined grains.
11
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - Weld Metal

More from these cases

ML00070 — Automotive Light Alloy Wheel Repaired By WeldingM - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Refined dendrites in the weld metal. The Si/Al alpha eutectic in the interdendritic space is also refined. Keller etch.
38
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Weld Metal
ML00055 — CA6NM Blade Remanufactured by WeldingM - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Weld metal micrography showing the tempered martensitic microstructure. It is possible to see previous austenite grain boundaries slightly marked.
12
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - Weld Metal
Micrographic detail of the weld metal presenting columnar grains and martensitic structure.
13
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Weld Metal
Higher magnification of the martensitic structure of the weld metal, in a region where the previous austenitic grains are columnar. Hardness level of 350HV10.
12
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Weld Metal
Micrographic detail of the weld metal presenting equiaxial grains grains and martensitic structure. There are also multiples globular inclusions, caracteristic of a welding process that uses flux.
10
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Weld Metal
Higher magnification of the martensitic structure of the weld metal, hardness level of 350HV10.
10
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Weld Metal