Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Finished Product Capture method: Transverse Section Aspect clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography of a transverse section of the fractured tooth. The tooth was cracked and the carburized layer was detached (left side of the image).
41
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Transverse Section AspectDf - Fatigue Crack
Transverse section of the tube in a position of localized thinning.
60
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Transverse Section AspectDf - Localized Thinning
Macrosection of the wire rope, transverse, showing 6 strands and an independent wire rope core (IWRC). Each strand presents three layers in a SEALE construction.
92
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Transverse Section AspectDf - Plastic Deformation
SCC of Austenitic SS Flange Stub End
1
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Transverse Section AspectDf - Cracks
Transverse section macrography of the plate where the degradation by thinning is worst, close to the original corners of the tube. The thinning is occurrring from the product reaction side (side A to the bottom of the figure). The macrography shows a reduction in the thickness from 2 mm (right side, sample 2) to almost zero (left side, sample 1).
86
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Transverse Section AspectDf - Thinning
The metallic part of the fork handle is about 9mm wide. It was cut in a transverse section and the profile is shown in this figure. The thickness is 1mm and the curvature depth is about 3mm.
86
VIEW
ML00151 / Dec.2018
Ferritic Stainless Steel of a Flatware Fork
M - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Cm - Transverse Section AspectDf - Formed Profile
Aspect of a section cut transverse to the center of the body. The crack is brittle, trough wall, and was arrested in the region where the valve body was welded to the insert.
105
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - Transverse Section AspectDf - Cracking
After a longitudinal cut of the case it was possible to see that a localized corrosion has occurred associated to the regions where there were sealed holes, plugged, in a crevice condition, not related to any welded position.
193
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Transverse Section AspectDf - Corrosion

More from these cases

ML00180 — Local Melting of Copper Cooling TubesM - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Transverse section of the tube in a position of wall perforation.
32
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Transverse Section AspectDf - Leakage
Local Melting of Copper Cooling Tubes
1
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Transverse Section AspectDf - Thinning
Local Melting of Copper Cooling Tubes
1
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Transverse Section AspectDf - Leakage
ML00175 — Localized External Wear of a Wire RopeM - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Detail of the IWRC with 6 strands of 7 wires plus the core. It is possible to see that the outer wires of the external strands are plastically deformed, mainly in the upper side of the figure; and the core is manufactured using galvanized wires.
39
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Transverse Section AspectDf - General View
Detail of the IWRC with 6 strands of 7 wires plus the core. It is possible to see that the outer wires of the external strands are plastically deformed, mainly in the upper side of the figure; and the core is manufactured using galvanized wires.
3
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Transverse Section AspectDf - General View
ML00134 — Brittle Fracture of a Superduplex Valve BodyM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Aspect of a section cut transverse to the center of the body. The structure of the valve body was not uniform and close to the BX groove body face the structure was more degradated than in the bottom of the body, as it will be presented in the next figures.
83
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - Transverse Section AspectDf - Cracking
Aspect of a section cut transverse to the center of the body. The cracking is brittle, trough wall.
58
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - Transverse Section AspectDf - Cracking
ML00122 — Crevice Corrosion in a Subsea SystemM - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Detail of the case thickness (20 mm) with the through wall localized corrosion in a crevice condition where there was a plug.
98
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Transverse Section AspectDf - Localized Corrosion